I agree. The flux makes a big difference.

 I regularly solder to nickel tabs that are spot welded to battery cells. I
played with various flux materials, the thick RMA flux from flux pens has
worked best. I have also solder coated by dipping in a solder pot, that RMA
works well.

 This always concerned me about ENIG, once the gold is dissolved off the
surface what happens next? 

 Bob K.


-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Glidden, Kevin
Sent: Thursday, August 29, 2013 3:01 PM
To: [log in to unmask]
Subject: Re: [TN] Solder joint failure

In my experience nickel is NOT easy to solder to at all.


-----Original Message-----
From: Victor Hernandez [mailto:[log in to unmask]]
Sent: Thursday, August 29, 2013 2:53 PM
To: [log in to unmask]
Subject: [TN] Solder joint failure

Fellow TechNetters:

   Should I be concern with an electroless matted nickel plating over an
aluminum sheet metal surface and solder onto a copper heat tube?   I recall
something about directly soldering onto a nickel surface.  Beside nickel
oxidation.    Any suggestions would be greatly appreciated.

Victor,

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________


______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________