I agree. The flux makes a big difference.
I regularly solder to nickel tabs that are spot welded to battery cells. I
played with various flux materials, the thick RMA flux from flux pens has
worked best. I have also solder coated by dipping in a solder pot, that RMA
works well.
This always concerned me about ENIG, once the gold is dissolved off the
surface what happens next?
Bob K.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Glidden, Kevin
Sent: Thursday, August 29, 2013 3:01 PM
To: [log in to unmask]
Subject: Re: [TN] Solder joint failure
In my experience nickel is NOT easy to solder to at all.
-----Original Message-----
From: Victor Hernandez [mailto:[log in to unmask]]
Sent: Thursday, August 29, 2013 2:53 PM
To: [log in to unmask]
Subject: [TN] Solder joint failure
Fellow TechNetters:
Should I be concern with an electroless matted nickel plating over an
aluminum sheet metal surface and solder onto a copper heat tube? I recall
something about directly soldering onto a nickel surface. Beside nickel
oxidation. Any suggestions would be greatly appreciated.
Victor,
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|