OK, what causes dewetting? It is caused by tinning a surface which is
inherently solderable, but has myriad unsolderable points of small
diameter. The commonest causes are the implantation of abrasive
particles in the base metal, co-deposition of organics in a badly
controlled plating process, gaps caused by epitaxial plating, selective
oxidation.
It could worry me, if the contacts in question overheated; have you
measured a significant temp difference between a dewetting and a
non-dewetting contacts at full current?
Brian
On 06.06.2013 21:59, Ed Popielarski wrote:
> Greetings fellow 'netters,
>
> I have discovered a dewetting condition on high current blade connector(s) which causes me to raise an eyebrow. I can't find any scholarly articles discussing the long term effect such an irregular surface at the material contact interface (photo located at http://stevezeva.homestead.com/Terminal_de-wetting.JPG ) will have on connection integrity at high current. This is an extreme environment automotive application with MTBF expectations in excess of 10 years.
>
> Any guidance and/or professional opinions would be greatly appreciated.
>
> As always, thanks to Steve G. for sharing his webspace with us!
>
> Ed Popielarski
> Engineering Manager
>
> [Description: FullLogo]
> 970 NE 21st Ct.
> Oak Harbor, Wa. 98277
>
> Ph: 360-675-1322
> Fx: 206-624-0965
> Cl: 949-581-6601
>
> https://maps.google.com/maps/myplaces?hl=en&ll=48.315753,-122.643578&spn=0.011188,0.033023&ctz=420&t=m&z=16&iwloc=A
>
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|