TECHNET Archives

May 2013

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Joyce Koo <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Joyce Koo <[log in to unmask]>
Date:
Thu, 30 May 2013 15:34:04 +0000
Content-Type:
text/plain
Parts/Attachments:
text/plain (26 lines)
Yap, someone took the cheap road: avoid selective plating. 

Joyce Koo
Researcher
Materials Interconnect Lab
Office: (519) 888-7465 79945
BlackBerry: (226) 220-4760

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Julie Silk
Sent: Thursday, May 30, 2013 11:28 AM
To: [log in to unmask]
Subject: Re: [TN] Gold Removal

Bev,  Our investigation into gold embrittlement with SAC started with parts that are wirebonded internally after several other heated process steps.  In order to have bondable gold at the end of those steps, there is a minimum of 30 uinches of gold required inside.  Of course with plating processes, the outside gets thicker plating, so the spec for these was 30 - 80 uinches (80!).  One of the original thoughts was that we would have to remove the gold by double-dip.  (Messy, expensive, adds to the supply chain and leadtime -- ick)  The first trials were lumpy plus damaged the parts.  We put that aside to work with the suppliers on their gold spec, but I figure the issue may come up again, and I'd like to hear if it's been tried or is possible.

Dave,  I do like that paper in JEM, authored by our own Mike Powers.  I'm not sure how small the joint would have to be for ENIG to be an issue -- especially with the Au thickness recommendation dropping.  I doubt this will be a problem.  I posted a Au calculation spreadsheet on the TechNet site a while back.  Could run through the numbers to see.

---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential information, privileged material (including material protected by the solicitor-client or other applicable privileges), or constitute non-public information. Any use of this information by anyone other than the intended recipient is prohibited. If you have received this transmission in error, please immediately reply to the sender and delete this information from your system. Use, dissemination, distribution, or reproduction of this transmission by unintended recipients is not authorized and may be unlawful.

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

ATOM RSS1 RSS2