Hi John,
If you have access, Ar ion beam etching is fantastic for revealing tin grain boundaries and wider joint microstructure (we can help if you need any support).
Kind regards,
Stewart
Stewart McCracken
Managing Director | MCS | Solving your Materials, Manufacturing and Reliability Issues
[log in to unmask] | www.themcsgroup.co.uk | +44(0)131 440 9090 | +44(0)771 154 1735
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of [log in to unmask]
Sent: 21 March 2013 14:53
To: [log in to unmask]
Subject: [TN] SAC 305 etch
What would a good etch be for etching SAC305 solder joints to enhance viewing grain boundaries?
Thanks,
John
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________