Ioan,

My guess is that most 'solder splashing' is a result of the flux activity (physical, not chemical). With that in mind, you might look at how much flux is being applied and when heat and solder are being applied (all at the same time?)

Ben

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Ioan Tempea
Sent: Friday, February 08, 2013 2:29 PM
To: [log in to unmask]
Subject: EXTERNAL: [TN] Anti-splashing solder wire

Dear Technos,

What do you think about this? Sounds pompous, but I wonder if this existed...

We noticed many solder balls and splashes on a particular board, after manual soldering or repairs/touch-ups and I wonder if there would be a particular brand/model of solder wire which is less splash prone.

Thanks,

Ioan Tempea, ing.
Ingénieur principal de fabrication / Senior Manufacturing Engineer [signature002]<http://www.digico.cc/>

950 RUE BERGAR, LAVAL, QC, H7L 5A1<http://g.co/maps/2gh3f>
T+ 1 (450) 967-7100, EXT244
------------------------------------------------------------------------
  [signature001] <http://www.facebook.com/pages/Digico/277076778479>
------------------------------------------------------------------------
Lauréat Dunamis 2012<http://digico.cc/dunamis-2012/>
Entreprise manufacturière / Gestion du capital humain


______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________