Dear Mr Reid,
Thank you for the reply. My understanding is if we polish too much , the fine copper smear may fill the separation and it will be very difficult to remove using microetch.
What is the optimum level of polishing, whether we have to go down to 0.03 microns or can we stop it 1 micron polish before microetch.
regards,
R.Saravanan