TECHNET Archives

May 2012

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Martin Bayes <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Martin Bayes <[log in to unmask]>
Date:
Wed, 30 May 2012 01:54:42 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (10 lines)
As others have already posted, conventional electrolytic nickel gold used as a PWB final finish,  uses a pure nickel underlayer.

It is worth noting that, for a number of other electronic component applications, electrolytic nickel-phosphorus is used commercially, rather than pure electrolytic nickel, due to its higher corrosion resistance. 

Such electrolytic nickel-phosphorus baths, typically operated at low bath pH (below 2) and contain hypophosphorous acid.  Co-deposition occurs in an analogous manner to electroless systems (with P-content controlled by variables including bath pH, hypophosphous acid content and current density). 

The development of modern day electroless nickel systems was triggered by the serendipitous discovery of electrolytic nickel phosphorus systems by Brenner and Riddell at what was then the National Bureau of Standards (now NIST) in the 1940's ( A. Brenner and G. Riddell, J. Res. N. B. S., (37), 32 (1946).

Martin