100,000 cycles of -55/+125C? Did the parts have representative die in them?
Scott Post
P.O.U. 0000-001E-0CTC
2151 E. Lincoln Road
Kokomo, Indiana 46904-9005
765-451-2983 (Phone)
765-451-0287 (FAX)
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Inge Hernefjord
Sent: Tuesday, April 03, 2012 2:24 PM
To: [log in to unmask]
Subject: Re: [TN] how to pass solder joint reliability of a 3.2 mm board (16 layers) for QFN packae
Can you develop your question so that a slow thinker like me can understand
TMCL 1000 c on QFN8's is very mild, I suppose nothing will happen. I
investigated QFN64's recently. They had passed 100,000 cycles with some few
issues. This was a -55/125 C test.
I think you should tell a little about the assembly, because that's what
decides the result.
Inge
On 2 April 2012 18:55, jonathan noquil <[log in to unmask]> wrote:
> Hi All
>
> Need some suggestions on how to handle solderjoint issue (How to tweak to
> pass TMCL1000 cycles- 0 to 100C) on QFN packages ( 5 x 6 x 1.0 mm with 8
> pins).
> Finish is Pure Sn
> Board is 16 layers 3.2 mm, HASL finish.
>
> Does someone had an experience to share?
>
> thanks
>
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
**************************************************************************************** Note: If the reader of this message is not the intended recipient, or an employee or agent responsible for delivering this message to the intended recipient, you are hereby notified that any dissemination, distribution or copying of this communication is strictly prohibited. If you have received this communication in error, please notify us immediately by replying to the message and deleting it from your computer. Thank you. ****************************************************************************************
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|