And it depends on your viewpoint - if your 401K is locked to the price of silver and tin you could I suspect take the viewpoint that it was a success......8-(
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Post, Scott E
Sent: Thursday, July 14, 2011 11:58 AM
To: [log in to unmask]
Subject: Re: [TN] Lead Free solder has performed well...
I agree that Pb free implementation hasn't been a disaster (with the exception of tin whiskers), but a few years without a bunch of major reliability catastrophes isn't a great indication of equivalent reliability. Besides the lack of time that's passed, especially for electronics requiring a long service life, there's also the fact that we've designed around some of the weaknesses of SAC alloys. For example, adding corner bond or underfill to pass BGA drop tests or using multiple smaller ceramic resistors in the place of one larger resistor to pass thermal cycling. If we'd left our designs alone and only changed the solder alloy we'd be seeing more reliability problems. In many situations Pb free is not as reliable as SnPb if everything but the alloy is kept equal.
Scott Post
Staff Manufacturing Engineer
P.O.U. 0000-001E-0CTC
2151 E. Lincoln Road
Kokomo, Indiana 46904-9005
765-451-2983 (Phone)
765-451-0287 (FAX)
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Eric Christison
Sent: Thursday, July 14, 2011 12:20 PM
To: [log in to unmask]
Subject: [TN] Lead Free solder has performed well...
http://www.designnews.com/author.asp?section_id=1389&doc_id=231199&f_src=designnews_gnews
"Dr. Ronald Lasky, Dartmouth professor of engineering and a frequent blogger on solder, claims the transition to lead-free was a grand success. “A lot of people claim that lead-free solder is not as reliable as lead-based solder,” Lasky told me. “We’re now five years into the implementation of RoHS, and we’ve made $3 trillion work of electronic.
We haven’t really noticed any big change in reliability.”"
I thought some of you may be interested in the above article.
Regards,
--
Eric Christison
Consumer& Micro group
Imaging Division
STMicroelectronics (R&D) Ltd
33 Pinkhill
Edinburgh EH12 7BF
United Kingdom
Tel: +44 (0)131 336 6165
Fax: + 44 (0)131 336 6001
The contents of the email are ST confidential.
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives For additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
**************************************************************************************** Note: If the reader of this message is not the intended recipient, or an employee or agent responsible for delivering this message to the intended recipient, you are hereby notified that any dissemination, distribution or copying of this communication is strictly prohibited. If you have received this communication in error, please notify us immediately by replying to the message and deleting it from your computer. Thank you. ****************************************************************************************
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|