Subject:
From:
Robert Kondner <[log in to unmask]>
Reply To:
Date:
Thu, 2 Jun 2011 11:58:24 -0400
Content-Type:
text/plain
Parts/Attachments:
text/plain (321 lines)
Bob,

 Thank you for the feedback. 

 Do you have any experience with Bi alloys used in some HASL vendors?  I
played with some a long time ago, spreading, temperature profile, they
behaved like Pb solders. 

Also: What am I (or the others) missing on this flatness issue. Do you think
it really is a non -issue once the boards are printed with solder paste?

Thanks,
Bob K.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bob METCALF
Sent: Thursday, June 02, 2011 11:45 AM
To: [log in to unmask]
Subject: Re: [TN] Best Board Finish - beyond gold

Bob,

As the surface for best solderability there is nothing better than a tin
lead solder finish. The only problem is a lot of the OEM's we deal with are
no longer accepting tin lead solder. The lead free solders in the HASL
environment has not gained as wide spread acceptance as everyone thought. 
ENEPIG is considered a "universal finish" that is compatible with a wide
range of applications so I see it gaining favor.

I do agree with you; if you can use tin lead HASL then I would go for that
in many applications.

Regards,

Bob Metcalf
Western Regional Manager

Atotech USA Inc
1750 Overview Drive
Rock Hill, South Carolina 29730 USA

Mobile: 714-334-7667
e-mail: [log in to unmask]
Internet: www.atotech.com

Managing Director: Kuldip Johal

This e-mail and any attachments hereto are business documents of Atotech USA
Inc. and may contain CONFIDENTIAL OR PROPRIETARY BUSINESS INFORMATION. 
 Unauthorized disclosure and/or use of information contained in this e-mail
are prohibited.  If you are not the intended recipient, you should dispose
of it and not use, disseminate or copy this message or any other files
transmitted with it.



.












From:   "Robert Kondner" <[log in to unmask]>
To:     "'TechNet E-Mail Forum'" <[log in to unmask]>, "'Bob METCALF'" 
<[log in to unmask]>
Date:   06/02/2011 08:37 AM
Subject:        RE: [TN] Best Board Finish - beyond gold



Bob,

 As for flatness: once a PCB has paste printed can you even tell what the
finish is? I have never been able to figure out this flatness thing.

 As for reliability I think solderability wins every time. Are you telling
me these other finishes have better solderability than, well solder, as
found only in a HASL finish? Has anyone ever seen "Black Pad" with HASL?
There is no Ni so the P cannot be wrong, ever. Right?

 I fell like a stick in the mud on my bias towards HASL, I am open to ideas
here. 

Bob K.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bob METCALF
Sent: Thursday, June 02, 2011 11:18 AM
To: [log in to unmask]
Subject: Re: [TN] Best Board Finish - beyond gold

When considering finishes, if the ultimate in reliability and surface
flatness are key considerations, you must give electroless nickel,
electroless palladium, immersion gold (ENEPIG) some consideration.

Regards,

Bob Metcalf
Western Regional Manager

Atotech USA Inc
1750 Overview Drive
Rock Hill, South Carolina 29730 USA

Mobile: 714-334-7667
e-mail: [log in to unmask]
Internet: www.atotech.com

Managing Director: Kuldip Johal

This e-mail and any attachments hereto are business documents of Atotech USA
Inc. and may contain CONFIDENTIAL OR PROPRIETARY BUSINESS INFORMATION. 
 Unauthorized disclosure and/or use of information contained in this e-mail
are prohibited.  If you are not the intended recipient, you should dispose
of it and not use, disseminate or copy this message or any other files
transmitted with it.



.












From:   "Stadem, Richard D." <[log in to unmask]>
To:     <[log in to unmask]>
Date:   06/02/2011 07:46 AM
Subject:        Re: [TN] Best Board Finish - beyond gold
Sent by:        TechNet <[log in to unmask]>



I agree with everything you say, Barbara. It sounds like you are now on your
way to making the correct choice.
Stay away from immersion tin.
If you choose immersion silver, refer to both IPC 1601 and IPC 4553 for
storage and handling considerations. They can be managed.
The double-sided process can leave a slight reduction of solderability with
immersion silver PWBs by the time you are ready to hand solder any PTH
parts, making that more difficult to do, sometimes.
That is why I asked.
Also, if you select Immersion Silver,  make sure that your PWB fabricator
has a good plating product, a well controlled process and some experience
with it.
Ditto with ENIG. Especially with ENIG.
Regarding immersion silver, it is susceptible to environments that are heavy
in sulfides, such as automotive exhaust, rubber processing, or paper
processing. Keep some of these things in mind both from an end-use
environment standpoint and from a storage standpoint. Do not store in areas
where there are open containers of soaps, fluxes, etc., nearby.

From: Barbara Burcham [mailto:[log in to unmask]]
Sent: Thursday, June 02, 2011 9:22 AM
To: Stadem, Richard D.
Cc: TechNet E-Mail Forum
Subject: Re: [TN] Best Board Finish - beyond gold

Thanks everyone for you imput. What a great group of people!

Richard,
The application will be double sided, fine pitch array components, some
through hole components and going into a shock environment.
I will need to connect with the assemblers to check on flux and paste
compounds. Does this information help?  You make an excellent point. Must
have the total picture. I do not know, yet, how long boards will sit on the
shelf before moving into assembly, either. I do know that shelf life will
also impact this decision.
I do not think that I want to use tin...that hairy growth stuff.
Barbara



On Thu, Jun 2, 2011 at 8:01 AM, Stadem, Richard D. <[log in to unmask]<
mailto:[log in to unmask]>> wrote:
Barbara,
What is the application, board type, component types, etc?
Immersion silver is my personal favorite, but that is completely 
irrelevant.
You should choose a board finish dependent upon the application of the 
CCA,
whether it has fine-pitch array components, including CSPs, whether it is
double-sided with PTH parts or hand-soldered components, the environment 
the
CCA will be used in, the flux type to be used, the alloy that is required,
and several other factors that go into the decision. 
Without complete knowledge of all these factors, it is hard for anyone to
answer that question. I can tell you that IAg beats ENIG in cost, but each
finish has strengths and weaknesses. Some definitely have more or less 
than
others.



-----Original Message-----
From: TechNet [mailto:[log in to unmask]<mailto:[log in to unmask]>] On Behalf 
Of
Barbara Burcham
Sent: Wednesday, June 01, 2011 8:17 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: [TN] Best Board Finish - beyond gold Hey Y'all, I am looking for 
a
reliable bare board finish that beats the cost of gold.
What experience is out there?
What would you recommend?
Thanks,
Barbara Burcham
pcb Trace Design
[log in to unmask]<mailto:[log in to unmask]>

______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]<
mailto:[log in to unmask]>
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0 To
unsubscribe, send a message to [log in to unmask]<mailto:[log in to unmask]
> with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]<mailto:[log in to unmask]>: SET Technet NOMAIL or (MAIL) To
receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives For
additional information, or contact Keach Sasamori at [log in to unmask]<
mailto:[log in to unmask]> or 847-615-7100 
ext.2815<tel:847-615-7100%20ext.2815>
-----------------------------------------------------


______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0 To
unsubscribe, send a message to [log in to unmask] with following text in the
BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per
day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------



______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0 To
unsubscribe, send a message to [log in to unmask] with following text in the
BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET 
Technet
NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send
e-mail to [log in to unmask]: SET Technet Digest Search the archives of
previous posts at: http://listserv.ipc.org/archives For additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------




______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------


______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2