Try using leadfree solder on Nuclear Power Plant..?
At 23:54 2011/5/12, Mike Fenner wrote:
>There are known compatibility issues with some alloys and joint
>configurations and in your case you would have determine the unknown ones.
>My question to you would be: Why go there?
>1) ROHS allows the use of leaded solders for repair of pre ROHS products.
>2) Infrastructure [power stations ] is presently excluded from ROHS along
>with anything else where high reliability is required (Aviation, medical,
>automotive etc).
>3) Suggest that even assuming Pb free solders were environmentally superior
>(and some doubt this), in your application the environmental impact of using
>Pb-free solders would be negligible and far outweighed by the possible
>consequences of unreliable joints.
>Regards
>
>
>Mike
>ü Please consider the environment before printing this e-mail
>-----Original Message-----
>From: TechNet [mailto:[log in to unmask]] On Behalf Of Goodyear, Patrick
>Sent: Sunday, May 01, 2011 7:12 AM
>To: [log in to unmask]
>Subject: [TN] Repair / Rework on non-in-house RoHS compliant boards
>
>As a technician that does frequent board level repair rework some
>questions have come to mind. While the majority of my work is legacy
>i.e. vintage (1968) we will face these concerns in the near future. The
>boards I primarly work on are Nuclear graded Class IE, (high
>reliability, seismically qualified, etc.) high dollar boards, typically
>in the 3-10g range and are not throw-aways, most have components that
>are no longer manufactured.
>I am looking to the industry to find best practices, this is one of the
>places that was suggested for posting. Any help you can give me would
>be appreciated.
>
>With pre RoHS solders most if not all of major manufacturers used 63/37
>solders and repair rework was easy, one just used 63/37.
>
>With the adoption of RoHS controls and the subsequent use of many
>different alloys of lead free solders, (at least 6 I know of), the
>following comes to mind:
>1. Are there compatibility issues mixing between the various alloys of
>lead-free employed currently in electronics manufactures? In strength
>and reliability primarly.
>2. How does the technician determine the correct alloy of lead-free
>solder to use?
>
>3. How does the technician determine what alloy was originally used by
>the manufacturer?
>
>4. Will IPC 7711A / 7721A standards be updated to delineate alloy
>determination and / or an alternate methods for the complete removal of
>lead-free solders and subsequent repair using 63/37 or lead-free alloys?
>Pat Goodyear
>Control Technician
>Pacific Gas and Electric Company
>Diablo Canyon Nuclear Power Plant
>PO Box 56
>Avila Beach, CA. 93424
>805-545-4312
>
>
>______________________________________________________________________
>This email has been scanned by the MessageLabs Email Security System.
>For more information please contact helpdesk at x2960 or [log in to unmask]
>______________________________________________________________________
>
>---------------------------------------------------
>Technet Mail List provided as a service by IPC using LISTSERV 16.0
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail to
>[log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>For additional information, or contact Keach Sasamori at [log in to unmask] or
>847-615-7100 ext.2815
>-----------------------------------------------------
>
>
>***This email, its content, and any files
>transmitted with it, are intended solely for the
>addressee(s) and may be legally privileged
>and/or confidential. If you are not the intended
>recipient, please contact the sender by return
>and delete the material from any computer. Any
>review, retransmission, dissemination, or other
>use of, or taking of any action in reliance upon
>this information by persons or entities other
>than the intended recipient is prohibited.
>
>Messages sent via this medium may be subjected
>to delays, non-delivery, and unauthorized
>alteration. This email has been prepared using
>information believed by the author to be
>reliable and accurate, but Indium Corporation
>makes no warranty as to accuracy or
>completeness. Indium Corporation does not accept
>responsibility for changes made to this email
>after it was sent. Any opinions or
>recommendations expressed herein are solely
>those of the author. They may be subject to change without notice.***
>
>
>______________________________________________________________________
>This email has been scanned by the MessageLabs Email Security System.
>For more information please contact helpdesk at x2960 or [log in to unmask]
>______________________________________________________________________
>
>---------------------------------------------------
>Technet Mail List provided as a service by IPC using LISTSERV 16.0
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of
>Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts:
>send e-mail to [log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>For additional information, or contact Keach
>Sasamori at [log in to unmask] or 847-615-7100 ext.2815
>-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 16.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
For additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|