Re: Vapour phase soldering?
From:
Julie Silk <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Julie Silk <[log in to unmask]>
Date:
Tue, 8 Feb 2011 14:36:54 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (17 lines) 
For the first, we use VPR at a couple of suppliers, Jabil and Venture, but they 
don't have the capability at all sites.

For the second, the concern is that the standard flux used in tin-lead paste 
typically will not survive 240C.  It will burn out and you won't get good joints.  
You can use tin-lead with higher temperature flux.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/ContentPage.aspx?Pageid=E-mail-Forums for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2