Subject:
From:
"David D. Hillman" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Thu, 18 Nov 2010 09:16:42 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (92 lines)
Hi Michelle! Are you cleaning the LED assembly/components in any manner? 
LEDs do not play well with many cleaning processes or cleaning 
chemistries.

Dave Hillman
Rockwell Collins
[log in to unmask]




Michelle Masaitis <[log in to unmask]> 
Sent by: TechNet <[log in to unmask]>
11/18/2010 07:41 AM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to
Michelle Masaitis <[log in to unmask]>


To
[log in to unmask]
cc

Subject
[TN] Led Failures Please help






-   the through-hole LED in question is made by company "EOI ", and their 
part number is  "EOZ-ZARNCD0-DG " (s 
-   according to the component spec sheet  (enclosed), the maximum 
temperature for the component is 260℃ 
-   the maximum temp and wave contact time we initially used is  249℃ , 
4-6 
seconds.  We saw some defects after first pass, usually about .2%, but one 

month as high as 1.5%.   After successful testing, there were then some 
latent defects that occurred at our customer or their end customer.  The 
defects are erratic, sometimes the LEDs work, and sometimes they don't 
-  the supplier recommended a lower temperature and shorter exposure 
profile 
so we used SAC305 solder with maximum temp of 244.4℃ and 3 seconds. 
There 
were no defects after first pass and testing, but again we had some latent 

defects occur at customer 
-   for reference, we run many similar LED from other manufacturers 
(OSRAM&Lumiled, also spec at 260℃) at temperatures of 251℃ and 4-7 
seconds 
and see no such problems. 

Attached is a wave profile.

Please let me know if you seen a similar issue and what caused it.


Thanks

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to 
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to 
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 
for additional information, or contact Keach Sasamori at [log in to unmask] or 
847-615-7100 ext.2815
-----------------------------------------------------



______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2