TECHNET Archives

October 2010

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Chris Mahanna <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Chris Mahanna <[log in to unmask]>
Date:
Mon, 11 Oct 2010 14:40:41 -0400
Content-Type:
text/plain
Parts/Attachments:
text/plain (85 lines)
Here are a few pictures
http://ipc-technet.groupsite.com/gallery/16011

this job is a mixed bag.  Currently we suspect soldering, cratering, ICT and t-cycling damage

Chris

From: [log in to unmask] [mailto:[log in to unmask]]
Sent: Monday, October 11, 2010 2:22 PM
To: TechNet E-Mail Forum; Chris Mahanna
Cc: [log in to unmask]
Subject: Re: [TN] Mech. damage or poor wetting?


Hi Chris - do you have any pictures you can share?

Dave Hillman
Rockwell Collins
[log in to unmask]

Chris Mahanna <[log in to unmask]>
Sent by: TechNet <[log in to unmask]>

10/11/2010 11:29 AM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to
Chris Mahanna <[log in to unmask]>


To

[log in to unmask]

cc

Subject

[TN] Mech. damage or poor wetting?







We have a BGA dye-n-pry job that shows board side sj damage with a strong correlation to fan-out clocking.
We also have some microsection evidence of poor wetting.
All damage/dye is on perimeters.

Is this an indication of heat sinking and subpar wetting, or can it be completely mechanical?  Both?

Thanks

Chris

______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2