Bob K,
I'm sure this will ignite a debate but personally, I wouldn't allow any of our boards to be assembled with "no-clean" solder paste. Perhaps Terry Munson can share with you some photos of why that's a bad idea. Not all the flux is inerted by the reflow process, so I'm advised.
Check out his website at http://residues.com/
This paper should give you some ideas
http://residues.com/pdfs/Circuits%20Assembly%20Articles/2004/low%20res/2004.03-The%20Key%20to%20Success%20-%20Circuits%20Assembly.pdf
Also this one
http://residues.com/pdfs/Circuits%20Assembly%20Articles/2003/low%20res/2003.03-Component%20Cleanliness%20in%20a%20No-Clean%20World%20-%20Circuits%20Assembly.pdf
I've visited Terry's facility in Kokomo, IN. He's got an incredible array of diagnostic instrumentation, some of which he has designed and manufactured himself (like the C3).
Bob Landman
H&L Instruments, LLC
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Robert Kondner
Sent: Wednesday, October 20, 2010 10:10 AM
To: [log in to unmask]
Subject: [TN] Cleanable Long Stencil Time Flux Question
Can anyone make a paste/flux suggestion?
In a past life I once used a No Clean Alpha Metal 6106 paste which had an incredibly long stencil life, I think it was 8 hours.
This stuff never really "Dried Out" and a pasted board could sit for two days and a "Missing Part" could thus be ordered and reflow soldered.
Trouble was NOTHING would remove this no clean flux and trying to wash messy THT or Rework flux could make a real mess.
Can anyone suggest a cleanable paste/flux that has a long stencil life and does not dry out to a hard crust?
Thanks,
Bob K.
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|