TECHNET Archives

September 2010

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
X-To:
TechNet E-Mail Forum <[log in to unmask]>, Rick Bell <[log in to unmask]>
Date:
Thu, 9 Sep 2010 05:59:44 -0500
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, "Stadem, Richard D." <[log in to unmask]>
Subject:
From:
"Stadem, Richard D." <[log in to unmask]>
MIME-Version:
1.0
In-Reply-To:
Content-Transfer-Encoding:
quoted-printable
Content-Type:
text/plain; charset="iso-8859-7"
Parts/Attachments:
text/plain (133 lines)
In all of this discussion I don't see any discussion about the type of paste. Type 4 solder paste will print through small apertures much better (much more uniformly, with less variation) than Type 3, which is the standard paste most companies use. I have used Type 5 and even Type 6 for certain applications where I need to reflow unbumped die to ASIC carriers. A WORD OF CAUTION HOWEVER. You better have your solder paste printer parameters screwed down tight before you attempt to use grain size smaller than Type 3, else you will end up with solder fines all over the board. Type 4 paste is usually not a problem to purchase, availability of Type 5 and smaller is special order, weeks in advance.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Rick Bell
Sent: Wednesday, September 08, 2010 4:06 PM
To: [log in to unmask]
Subject: Re: [TN] Stencil thickness v solder paste height

Trick question?

If the AAR of the aperture is poor (on a 0.1mm nominal foil, it'd have to be pretty small-- maybe a 0.2mm round or less), you can get zero height on the board.  Literally all of the solder paste stays in the aperture.

It probably goes without saying, but that can also happen if you have so much of a gap that the paste deposit doesn't touch the board.  I've seen it on flex circuits with integrated stiffeners.

And yes, you can get a localized height above that of the stencil depending on the rheology of the paste, but it won't be uniform.  The deposits I've seen affected in that manner are usually tallest in the center.  You could also conceivably get an "extra-thick" solder deposit height by using a couple mils of snapoff and enough squeegee pressure to inject the paste through the aperture and onto the pad.  I'd expect print quality to be really poor with no gasketing, though.

The 3D paste inspection guys will tell you that's why it's critical to measure total printed volume on the pad, rather than height or area.



___________________________________________________________________________________________________________________________________________
This email and any attachments are only for use by the intended recipient(s) and may contain legally privileged, confidential, proprietary or otherwise private information. Any unauthorized use, reproduction, dissemination, distribution or other disclosure of the contents of this e-mail or its attachments is strictly prohibited. If you have received this email in error, please notify the sender immediately and delete the original.
 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Eric Christison
Sent: Tuesday, September 07, 2010 3:24 AM
To: [log in to unmask]
Subject: Re: [TN] Stencil thickness v solder paste height

Thanks Bob,

A quick look tells me that solder paste volume can vary by +/-50% which 
seems a lot. Is it reasonable to assume that the blob height will never 
be more than the height of the stencil or can the edges be pulled 
upwards when the stencil is lifted?

Regards,



On 06/09/2010 19:20, Robert Kondner wrote:
> Eric,
>
>   Good question, if you look at the web sites for folks that vend 3D paste
> inspection system I bet you can find some good data.
>
>   What I have seen is the surface of the PCB is not flat, solder mask and
> silk screen ink act like hold offs at time. Tented vias for big high blobs.
>
>   And, of course, there is scoping of paste from plastic squeegees.
>
> Bob Kondner
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Eric Christison
> Sent: Monday, September 06, 2010 11:02 AM
> To: [log in to unmask]
> Subject: [TN] Stencil thickness v solder paste height
>
> I guess this is an easy one for most you...
>
> If solder paste is applied to a PWB with a 0.10+/-0.01mm thick stencil
> what is the minimum height of paste I can expect to get on the PWB?
>
> Sn95.5Ag3.8Cu0.7 paste , DAP (20 - 38 ìm) or Sn95.5Ag4.0Cu0.5, IPC type
> 3 (25-45 ìm) if composition makes much difference.
>
> Thanks,
>
>    

-- 
Eric Christison
Consumer&  Micro group
Imaging Division

STMicroelectronics (R&D) Ltd
33 Pinkhill
Edinburgh EH12 7BF
United Kingdom

Tel:	+44 (0)131 336 6165
Fax:	+ 44 (0)131 336 6001




______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2