Ti = Fit & Forget
That is the replacement!
:-)
Rex
Sent by me
On 6 Aug 2010, at 14:13, "[log in to unmask]" <[log in to unmask]> wrote:
>
> Hi Rex - it appears that the Melonite coating was compromised. I know that Ti is more expensive but it has been shown to handle the degradation by molten tin much better. Something to consider.
>
> Dave Hillman
> Rockwell Collins
> [log in to unmask]
>
>
> Rex Waygood <[log in to unmask]>
> Sent by: TechNet <[log in to unmask]>
> 08/06/2010 06:47 AM
>
> Please respond to
> TechNet E-Mail Forum <[log in to unmask]>; Please respond to
> Rex Waygood <[log in to unmask]>
>
> To
> [log in to unmask]
> cc
> Subject
> Re: [TN] Wave Corrosion
>
>
>
>
>
> I forgot to say the impeller was a retrofit on the machine.
> Rex
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Rex Waygood
> Sent: 06 August 2010 12:14
> To: [log in to unmask]
> Subject: Re: [TN] Wave Corrosion
>
> Ummm
> The website crashed just after I put the images up, obviously the site
> didn't like my pictures either.
> As far as I know the surface treatment used is Melonite QPQ.
> Regards
> Rex
>
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
> Sent: 06 August 2010 12:09
> To: [log in to unmask]
> Subject: Re: [TN] Wave Corrosion
>
> Hi Rex!
>
> Your link appears to be broken. I would have liked to seen the photos.
> Was the machine brand new or was it retrofitted to be lead free
> compatible? Do you know what the impeller was made of? Or was it coated
> to protect it from high tin content solder?
>
> Steve
>
>
>
> ______________________________________________________________________
>
> ______________________________________________________________________
> This email has been scanned by the MessageLabs Email Security System.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
>
>
> ______________________________________________________________________
> This email has been scanned by the MessageLabs Email
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|