Looks almost like one is FR-4 and the other is Polyimide. There was mention 
that they are from different lots. Call the supplier and see. Perhaps they 
(the board supplier) messed up and pulled one sheet of Polyimide and figured 
that it would be okay to send based on the fact it met or exceeded 
requirements per print.
Dan S.
----- Original Message ----- 
From: "Steve Gregory" <[log in to unmask]>
To: <[log in to unmask]>
Sent: Thursday, July 29, 2010 9:34 PM
Subject: Re: [TN] PCB Discoloration


> Hi Linda!
>
> While discoloration in itself is not a defect, I would be a little worried 
> about these seven boards. Especially since the rest of the lot are not 
> discolored like this:
>
>
> http://stevezeva.homestead.com/PCB_Discoloration1.jpg
>
>
>
> I don't see any delamination in the photos, but it sure looks like the 
> boards got pretty toasty. I wonder if it was because the boards were 
> sitting over a preheater or hot plate too long. From the looks of the 
> components on the board, most of it was probably hand soldered (those PTH 
> caps converted to SMT couldn't have taken reflow), and I imagine that the 
> solid plane on on the backside of the board was a real heatsink. 
> Preheating the board would have helped with soldering the PEM nuts for 
> sure, but maybe the preheater was set too high. I know a Hakko IR 
> preheater can smoke a board if you're not careful (not that I've ever done 
> that, but I know a friend of a friend who did. Hehehehe).
>
>
>
> Anyways, those seven boards saw more heat than the rest of them did based 
> on the appearance in the photos. I don't think I'd buy off on them...
>
>
>
> Steve
>
>
>
>
>
>
>
> From: Linda Langley [mailto:[log in to unmask]]
> Sent: Thursday, July 29, 2010 1:42 PM
> To: Steve Gregory
> Subject: FW: PCB Discoloration
>
>
>
> Hi Steve,
>
>
>
> Here I go again asking for help from my experts! Can you please post these 
> pictures? So I don’t have to bother the whole forum, would you know the 
> name of the board guru that could answer my questions?
>
>
>
> I am not sure if the discoloration is a defect, is this a form of 
> delaminating? Why would only seven boards turn this color? They are all 
> from the same lot.
>
>
>
> Any information will be greatly appreciated.
>
>
>
>
> Linda Langley CIT
>
> Training Specialist
>
> Jabil Circuit
>
> 248-292-6176
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to 
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to 
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 
> for additional information, or contact Keach Sasamori at [log in to unmask] or 
> 847-615-7100 ext.2815
> -----------------------------------------------------
> 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------