Hi,
A Question:
I would think, and I might be wrong, that once water is in a vapor form it
would pretty much follows the ideal gas law. So, would water vapor in a PCB
structure behave much like air or any other gas? Is that correct?
Would an air filled section of a PCB generate pressures equivalent to water
filled areas?
Bob Kondner
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Paul Edwards
Sent: Thursday, July 15, 2010 3:22 PM
To: [log in to unmask]
Subject: Re: [TN] BAKING OF PWB QUESTION
I'm with Werner on this...
I am concerned with the general statements made that:
"Basically we are saying that many studies demonstrate limited impact,
positive or negative, on reliability due to baking. Dr. Taube shows
"moisture in" or "moisture out" has a limited reliability affect. The effect
of baking is not compelling for extending ability to survive assembly and
rework."
I can tell you that numerous assemblies and reworks have been done
successfully due to the pre-baking of components, PCBs and assemblies...
We have run both no bake and pre-baked processes and found consistently that
the pre-baked materials always yields higher finished product...
If baking out moisture did not increase reliability then there would be no
detrimental effect to the unlimited exposure of non-ceramic BGAs to
moisture...After all most BGAs use a PCB-like substrate...
Paul
Paul Edwards
Surface Art Engineering
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Werner Engelmaier
Sent: Thursday, July 15, 2010 12:01 PM
To: [log in to unmask]
Subject: Re: [TN] BAKING OF PWB QUESTION
Hi Paul,
I think we went over the water vapor/steam issue once before.
It simply is not so that one needs liquid water to have an increase in
pressure.
Consider a closed vessel with some water in it. As you heat the vessel the
liquid water will vaporize until all of it has vaporized. Just because you
no longer have liquid H2O does not mean that the pressure does not increase
with increasing T-you now have superheated steam that follows the equation
P= RT/V-so the higher the temperature the higher the pressure for a constant
volume. V certainly can increase with delamination and some of the
superheated steam will escape. The term 'live steam' has no meaning in this
context-its primary use is for model railroading, and refers to steam
actually doing some work in driving the locomotive. Inside the PCB, liquid
water per se does hardly ever exist, the steam does do 'work' only in terms
of increasing the internal vapor pressure, and you certainly do not need
liquid water for that.
Werner
-----Original Message-----
From: Paul Reid <[log in to unmask]>
To: [log in to unmask]
Sent: Thu, Jul 15, 2010 11:37 am
Subject: Re: [TN] BAKING OF PWB QUESTION
This is a good thread.
Off-line Ian Hanna from Circuit Tech comments:
"Hey Paul, I would expect that the biggest threat from trapped moisture is
the
vapour pressures generated during the initial shock of assembly...would this
be
visible during cyclic reliability testing? Regards - Ian"
The answer to Ian's question is, yes, the greatest "threat" (or at least
pressure) from trapped moisture is during the initial thermal excursion and
yes
it is visible during reliability testing. But no we do not see delamination
during the first thermal cycle and if the material delaminates the effect is
extended cycles to failure. The lesson is you have to test both the copper
and
the material when doing reliability testing for lead/free applications
incase
the material degrades and you get false positives from thermal cycle
testing. We
measure material damage by means of changes in capacitance in representative
coupons in order to capture material damage.
Basically we are saying that many studies demonstrate limited impact,
positive
or negative, on reliability due to baking. Dr. Taube shows "moisture in" or
"moisture out" has a limited reliability affect. The effect of baking is not
compelling for extending ability to survive assembly and rework.
The idea is that vapor pressure from trapped water "blows" the material
apart.
It is my contention that if the adhesion between laminated surfaces is weak,
by
that I mean, between B-stage and C-stage or B-stage and copper, then vapor
pressure generated from trapped water may cause frank delamination. But
there is
more to this story.
I expect the greatest pressure from water vapor would occur during heating
on
the first thermal excursion because the board has the greatest amount of
water
at the beginning of assembly. After the first cycle moisture must have been
out
gassing during the thermal excursion. The longer at temperature the less
water
in the board so by the second thermal excursion there should be less
pressure
because some of the water has been lost. Our findings are consistent with
Dr.
Taube's findings. Delamination does not typically occur on the first thermal
cycle. Delamination frequently occurs after the third thermal excursion.
Let's
let that stand for a second.
Dr. Wayne Rothschild points out that the vapor pressure is limited by the
amount
of water available to the system. He points out that the gas laws take into
account the amount of water in the system.
Pressure increases rapidly with "live steam" but, when the water is all
vaporized, the pressure increase is reduced. "Live steam" requires liquid
water
as a source to replace the steam. A steam train stops when it runs out of
water.
The vapor pressure goes to zero once the water escapes out of the board.
So bringing Dr. Taube's and Dr. Rothschild's observations, our experience in
reliability testing, and how samples fail in T260 testing on a TMA,
together, I
feel that the damage to material is from vapor pressure, z-axis expansion
and
also material degradation. The epoxy system is failing and volatiles are
providing a force as is z-axis expansion of the epoxy system, to a point
were
force is greater than the strength of the epoxy and the board fails. Epoxy
degradation is a major component of the failures and aggressive baking could
degrade the epoxy reducing reliability in a lead/free application.
All this stands given that the copper is not being degraded by 260°C, which
I,
and others are beginning expect it is changing, when the copper is poorly
plated
and of a lower quality. But that is another story.
Sincerely,
Paul Reid
Program Coordinator
PWB Interconnect Solutions Inc.
235 Stafford Rd., West, Unit 103
Nepean, Ontario
Canada, K2H 9C1
613 596 4244 ext. 229
Skype paul_reid_pwb
[log in to unmask] <mailto:[log in to unmask]>
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
============================================================================
==
This email and any attachments thereto may contain private, confidential,
and
privileged material for the sole use of the intended recipient. Any review,
copying,
or distribution of this email (or any attachments thereto) by others is
strictly prohibited.
If you are not the intended recipient, please contact
[log in to unmask]
immediately and permanently delete the original and any copies of this email
and
any attachments thereto.
============================================================================
==
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|