Make it a third...
Had to deal with the finish dewetting problems by setting use-by, store-in and bake-in-N2 rules for using the PCBs....
Paul
Paul Edwards
Surface Art Engineering
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Wenger, George M.
Sent: Wednesday, June 30, 2010 4:14 PM
To: [log in to unmask]
Subject: Re: [TN] Bright tin
Dave,
I'll be the second dissenter right behind you.
Regards,
George
George M. Wenger
Senior Principal FMA / Reliability Engineer Andrew Corporation - Wireless Network Solutions 40 Technology Drive, Warren, NJ 07059
(908) 546-4531 Office (732) 309-8964 Mobile
E-mail: [log in to unmask]
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman
Sent: Wednesday, June 30, 2010 5:27 PM
To: [log in to unmask]
Subject: Re: [TN] Bright tin
Hi Rudy - I guess I'll be the voice of dissent but I would run as far away from bright tin as fast as possible. The industry studies demonstrating bright tin's ability to initiate and growth tin whiskers making a plated object look like a chia pet are numerous. Additionally, the co-deposited organic materials in a bright tin plated finish typically result in outgassing during soldering resulting in poor solder joints of questionable integrity. Steve G. had a picture several months back of the result of trying to solder a bright tin plated connector. Finally, bright tin has poor solderability shelf life issues (as you detailed) due to oxidation issues. I recommend not allowing the use of bright tin on pwbs.
Dave Hillman
Rockwell Collins
[log in to unmask]
R Sedlak <[log in to unmask]>
Sent by: TechNet <[log in to unmask]>
06/30/2010 01:05 PM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to R Sedlak <[log in to unmask]>
To
[log in to unmask]
cc
Subject
Re: [TN] Bright tin
Cedric:
Bright Tin is definitely electroplated, and as such can be much thicker
than the more common immersion Tin, however, since it is electroplated, it
covers the top of the pad, and there may be exposed Copper on the sides of
the pad.
Bright Tin is high in organics, which should minimize, but not eliminate,
Tin whiskers.
Nickel is normally not used under Bright Tin, although it MIGHT help shelf
life. Shelf life of Bright Tin finish is more controlled by oxide
formation on surface of Tin, rather than by intermetallic formation,
because the Tin is usually so thick.
Hope this assists.
Rudy Sedlak
RD Chemical Company
--- On Wed, 6/30/10, Cedric ORAIN <[log in to unmask]> wrote:
From: Cedric ORAIN <[log in to unmask]>
Subject: [TN] Bright tin
To: [log in to unmask]
Date: Wednesday, June 30, 2010, 10:03 AM
Hello all,
I've been proposed Bright Tin as PCB finishing. It is the first time I've
heard about this plating for PCB.
Is someone is familiar with this process and could expose drawbacks and
benefit?
Do you confirm that it is an electroplating process? Do I need to specify
a
Nickel barrier or something lie that underneath the tin layer? Is the
thickness of tin is critical and has to be monitored carefully?
I'm also concerned about tin whiskers with bright tin as it as been banned
from the plating of connectors and components due to its propensity to the
growth of whiskers.
Ok, it's a lot of questions! I just want to be advised on what is
important
to know about that subject.
Thanks in adavance for your bright advice.
Cedric ORAIN
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
==============================================================================
This email and any attachments thereto may contain private, confidential, and
privileged material for the sole use of the intended recipient. Any review, copying,
or distribution of this email (or any attachments thereto) by others is strictly prohibited.
If you are not the intended recipient, please contact [log in to unmask]
immediately and permanently delete the original and any copies of this email and
any attachments thereto.
==============================================================================
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|