Jack,
Just designing for RoHS compliance does not dictate the use of non-dicey
cured material. If you are designing a fully compliant, complex,
Lead-free design that will be exposed to a minimum of two lead-free
reflow profiles and one wave solder operation and expect it to work for
twenty plus years, then no dicey-cured FR4 shall apply. IPC-4101/126 and
/129 are phenolic cured materials which have demonstrated a robustness
that is up to the challenge.
Dewey
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Jack Olson
Sent: Tuesday, May 18, 2010 2:29 PM
To: [log in to unmask]
Subject: [TN] My first RoHS circuit board!
Well, we avoided it as long as we could, but now I have to design for
RoHS
compliance.
I'm basically following Werner's recommendations (which don't conflict
with
anyone else's as far as I know), but I'm confused about one aspect of
material:
Several sources have stated that its better to use "NON-DICEY" material,
but
none of the IPC-4101 slash sheets mention dicy or non-dicy (or
dicyandiamide).
If we are trying /126 material, do we still have to specify non-dicy?
thanks,
Jack
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or
[log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|