With all the respect for your oustanding knowledge here, but we found that
the fine grain zone closest to the lead was much cleaner while the coarser
structure had lots of inclusions (e.g. dross), traces of iron and copper
between the grain borders and other imperfections. We draw the conclusion
that the difference between these two regions caused a somewhat weaker zone
(more sensitive to stress) We shifted to variations in the cooling rate, and
were very satified to see that the time to failue increased a lot with
decreasing the cooling time significantly! But Siemens did not say Thank you
for the help....but that's another story.
Inge
----- Original Message -----
From: "David D. Hillman" <[log in to unmask]>
To: <[log in to unmask]>
Sent: Tuesday, April 27, 2010 10:43 PM
Subject: Re: [TN] Failure fatigue photos
Hi Inge - you don't necessarily need to have a microstructure
solidification gradient grain size. Thermal and vibrational induced
stresses can change a completely uniform microstructure to a banded
microstructure. The IPC will be soon publishing the IPC -AJ-820 Assembly &
Joining handbook which has several good photos plus verbiage of banded
microstructure.
Dave
"Inge" <[log in to unmask]>
04/27/2010 03:22 PM
Please respond to
"Inge" <[log in to unmask]>
To
<[log in to unmask]>, <[log in to unmask]>
cc
Subject
Re: [TN] Failure fatigue photos
Hi both of you,
I made a job for Siemens once, about fatigue. The board behind the
instrument panel of a truck vibrated on the roads in South America,
resulting in lifted leads and the trucks became inoperable. I simulated
the
situation in the vibrator lab, and could see clearly what happened. Just
as
Dave told you, the crack will finally occur in a band which is represented
by fine structure on the one side and a coarse and elongated on the other.
It has partly to do with the solidification to do, fine grains closest to
the legs and coarser the more you are from that site. I'll send one very
illustrative photo. I've missed how to fix that instantly. How do you
bring
the photos to that fast presentation URL?
Inge
--------------------------------------------------
From: "David D. Hillman" <[log in to unmask]>
Sent: den 27 April 2010 06:33
To: <[log in to unmask]>
Subject: Re: [TN] Failure fatigue photos
> Hi Ioan - Do you have any optical photos of the fracture? Thermal cycle
> fatigue failures typically develop "banding (aka microstructure
> coarsening)" in the solder joint shear zone. The solder joint
> microstructure evolves into distinct grains of tin and lead which shows
up
> better in optical photos. The fracture in your photos appears to be
> fatigue but its hard to see the microstructure in your photos. I added a
> photo of what typical thermal cycle induced SnPb coarsening looks like
on
> the IPC Photo Gallery.
>
> http://ipc-technet.groupsite.com/gallery/13118
>
> Dave Hillman
> Rockwell Collins
> [log in to unmask]
>
>
>
> Ioan Tempea <[log in to unmask]>
> Sent by: TechNet <[log in to unmask]>
> 04/27/2010 07:59 AM
> Please respond to
> TechNet E-Mail Forum <[log in to unmask]>; Please respond to
> Ioan Tempea <[log in to unmask]>
>
>
> To
> [log in to unmask]
> cc
>
> Subject
> [TN] Failure fatigue photos
>
>
>
>
>
>
> Dear Technos,
>
>
>
> It looks like, for the first time, I have the occasion to look at
fatigue
> failed joints. The lab analysis we've got states this, but does not
> abounds in details.
>
>
>
> One of the conclusions is "the crack propagates around harder Sn
shearing
> the softer Pb, but the Sn and Pb zones seem fairly large for regular
> solder structure". Citing from Klein Wassink "During cyclic plastic
> deformation the microstructure inside the material changes in the zones
> where the deformation is concentrated. This leads to local grain
> growth..."
>
>
>
> I have deposited the micro-sections on the IPCs website
> http://ipc-technet.groupsite.com/gallery/13116
>
>
>
> I would need your expert opinion regarding the failure. Is this fatigue?
> The big pure Sn and pure Pb areas, are they normal size for fatigued
> joints?
>
>
>
> Thanks,
>
>
>
> Ioan Tempea, ing.
> Ingénieur Principal de Fabrication / Senior Manufacturing Engineer
> T | 450.967.7100 ext.244
> E | [log in to unmask] <mailto:[log in to unmask]>
> W | www.digico.cc <http://www.digico.cc/>
>
>
> N'imprimer que si nécessaire - Print only if you must
>
>
>
>
> ______________________________________________________________________
> This email has been scanned by the MessageLabs Email Security System.
> For more information please contact helpdesk at x2960 or
[log in to unmask]
> ______________________________________________________________________
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text
in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
http://listserv.ipc.org/archives
> Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at [log in to unmask]
or
> 847-615-7100 ext.2815
> -----------------------------------------------------
>
>
> ______________________________________________________________________
> This email has been scanned by the MessageLabs Email Security System.
> For more information please contact helpdesk at x2960 or
[log in to unmask]
> ______________________________________________________________________
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text
in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
http://listserv.ipc.org/archives
> Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at [log in to unmask]
or
> 847-615-7100 ext.2815
> -----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|