Hello Tech,

We performed HATS test on some PCB`s vendors using a few PCB
technologies. Will it be reasonable to define Pass/Fail criteria for
Avionic systems as  10%/500 cycles after 6 eutectic solder simulations
using -40 to 145C? What are the criteria's you are using? Is it a tough
demands or should most PCB class 3 pass it?

Thanks,

Gil Zilber
Elta Systems

 The information contained in this communication is proprietary to Israel Aerospace Industries Ltd., ELTA Systems Ltd. 
and/or third parties, may contain classified or privileged information, and is intended only for 
the use of the intended addressee thereof. If you are not the intended addressee, please be aware 
that any use, disclosure, distribution and/or copying of this communication is strictly prohibited.
If you receive this communication in error, please notify the sender immediately and delete it from 
your computer. Thank you. 


This message is processed by the PrivaWall Email Security Server. 




______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------