Subject:
From:
Victor Hernandez <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Wed, 4 Nov 2009 14:21:48 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (177 lines)
Could you have a plugged stencil aperture?   No solder paste the solder
bump will not collapse.

Victor,

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Paul Edwards
Sent: Wednesday, November 04, 2009 2:11 PM
To: [log in to unmask]
Subject: Re: [TN] BGA Balls - Found word(s) remove list in the Text body

Rex,

Have seen BGAs with balls separating from the substrate side...

Have seen the balls sitting in the trays for the devices...

My guess is that the BGA substrate has a Ni-Au surface finish...

The PCB side adhesion problems will sometime show up on the BGA
substrate side for similar reasons...
If the balls you removed have no solder wetting to the BGA substrate and
they are very smooth and light gray, I think you have a BGA substrate
problem

You can partially confirm this by having the pads of BGAs you removed
cleaned and re-tinned then reballed and reinstalled in the PCAs...

This works in most cases except when you have a bad chip...

Paul


Paul Edwards
Surface Art Engineering


-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Rex Waygood
Sent: Wednesday, November 04, 2009 8:36 AM
To: [log in to unmask]
Subject: [TN] BGA Balls - Found word(s) remove list in the Text body

We have built a batch of pcbs for a customer who supplied the pcbs. They
are 2mm thick 6 layer with 0.2mm vias and ENIG finish. None work fully,
they work intermittently at best.

The customer was suspicious that we had not reflowed the BGAs correctly.

Our under BGA temp on a similar pcb is 245C (We now have some samples to
profile correctly)

The customer is suspicious due to the comment on page 753
http://www.atmel.com/dyn/resources/prod_documents/doc6221.pdf
<http://www.atmel.com/dyn/resources/prod_documents/doc6221.pdf>  where
it states a min of 250C

Close x-ray evaluation of the BGAs showed tear dropping along tracks,
uniform balls, everything looked tickety boo.

We offered to remove a BGA to see what was happening underneath.

2 corners showed a similar issue with the ball where it separated from
the BGA rather than the pcb.

The removal technique was to use a PDR IR rework station, under board
heating to bring topside pcb temp to 170C and then a lead free reflow
profile to bring the device up to reflow, manual removal.

I didn't have dye for dye and pry so thought this might show if there
was an ENIG problem.

I was surprised by the almost complete removal of ball at the device and
lack of evidence of solder.

Was this just caused by my investigation processes?

Was the ball device interface broken which prevented it from melting the
ball?

Any other clues?

Thanks

Rex



Hopefully Steve has received the images (sorry about the size!)


Rex Waygood
Technical Manager

Hansatech EMS provides value manufacturing through engineering and
quality

________________________________


Hansatech EMS Limited
Benson Road
Nuffield Industrial Estate
Poole
Dorset BH17 0RY
United Kingdom


Tel:
Fax:
DDI:    +44 (0)1202 338200
+44 (0)1202 338202
+44 (0)1202 338222
[log in to unmask]
www.HansatechEMS.com <http://www.hansatechems.com/>


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------


========================================================================
======

This email and any attachments thereto may contain private,
confidential, and
privileged material for the sole use of the intended recipient. Any
review, copying,
or distribution of this email (or any attachments thereto) by others is
strictly prohibited.
If you are not the intended recipient, please contact
[log in to unmask]
immediately and permanently delete the original and any copies of this
email and
any attachments thereto. 

========================================================================
======


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2