Subject:
Re: Ductility of nickel
From:
Inge <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Inge <[log in to unmask]>
Date:
Sat, 17 Oct 2009 20:22:47 +0200
Content-Type:
text/plain
Parts/Attachments:
text/plain (157 lines) 
Hi Dave,

You are right (as usual). I have Safranek's plating bible, and there you can 
see all variations that you mention.
/Inge


----- Original Message ----- 
From: "David D. Hillman" <[log in to unmask]>
To: <[log in to unmask]>
Sent: Friday, October 02, 2009 2:18 PM
Subject: Re: [TN] Ductility of nickel


> Hi Inge! Yep, the elongation is dependent on which type of nickel plating
> bath used (i.e. Chloride, Fluoborate, Sulfamate, Nickel-Cobalt, etc) but
> the values range from 10-30% per Table 1, page 314, in Modern
> Electroplating, F. Lowenheim, ISBN 0-471-54968-1.
>
> Dave
>
>
>
> Hernefjord Ingemar <[log in to unmask]>
> 10/02/2009 03:56 AM
>
> To
> TechNet E-Mail Forum <[log in to unmask]>, "[log in to unmask]"
> <[log in to unmask]>
> cc
>
> Subject
> RE: [TN] Ductility of nickel
>
>
>
>
>
>
> Dave,
>
> 10-30% !  Are you serious? Like Copper? I had no idea.
>
> Inge
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman
> Sent: torsdag 1 oktober 2009 22:07
> To: [log in to unmask]
> Subject: Re: [TN] Ductility of nickel
>
> Hi Steve - I can't seem to put my fingers on the references but I believe
> that the elongation of High Phos Enickel is 1-1.5% and the elongation of
> electroplated nickel ranges from 10-30%. Good Luck.
>
> Dave Hillman
> Rockwell Collins
> [log in to unmask]
>
>
>
>
> Steve Kelly <[log in to unmask]>
> Sent by: TechNet <[log in to unmask]>
> 10/01/2009 02:43 PM
> Please respond to
> TechNet E-Mail Forum <[log in to unmask]>; Please respond to Steve Kelly
> <[log in to unmask]>
>
>
> To
> [log in to unmask]
> cc
>
> Subject
> [TN] Ductility of nickel
>
>
>
>
>
>
> Hi All,
>
> What is the approximate difference in ductility between electroless nickel
> (as used in an ENIG line - mid phos- 40 -80 micro inches in thickness) and
> the same amount as electroplated to QQN-290. Thanks. Steve Kelly
>
>
>
> Steve Kelly (PLEASE NOTE NEW E-MAIL ADDRESS)
>
> (416) 750-8433 (work)
>
> (416) 750-0016 (fax)
>
> (416) 577-8433 (cell)
>
>
>
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
>
> for additional information, or contact Keach Sasamori at [log in to unmask] or
>
> 847-615-7100 ext.2815
> -----------------------------------------------------
>
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at [log in to unmask] or
> 847-615-7100 ext.2815
> -----------------------------------------------------
>
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to 
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to 
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 
> for additional information, or contact Keach Sasamori at [log in to unmask] or 
> 847-615-7100 ext.2815
> ----------------------------------------------------- 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2