Technetters,
We have a problem with non wetting on a very specific component. Only
this part exhibits the problem. These are double stacked FLASH TSOP
components that are stacked from the vendor.
http://stevezeva.homestead.com/files/test6.jpg shows the same pin as in
test7 but enlarged.
http://stevezeva.homestead.com/files/test7.jpg shows the most extreme
case with no heal fillet.
http://stevezeva.homestead.com/files/test8.jpg hows another example with
a heal and toe fillet, but there is a crease on both sides of the pin
The process is lead free. Our peak is about 245 for these components. We
hold peak for 20-30 sec. TAL is about 70. I can not run much hotter
since there are large (676 pin) BGAs that reach 260. We have been all
over the spectrum with respect to profile. My revision log shows I have
done about 25 different ones. We have tried long soak, medium soak and
short hot ramp to spike. We have also experimented with different solder
types. The winner so far is a Water Soluble SAC305. The best results
(least defects) do come with a shorter RTS profile. The FLASH vendor
recommends we peak and hold at 255 -260 for ~30 sec. I am not able to do
that since then the 672 pin BGAs (3 of them) reach well above the
recommended temp of 250. With the current profile they are already at
260. As you have already guessed, there is a 10 - 15 degree delta on
this board that is very heavily populated with these TSOPs. This board
has in other words a large mass. This condition does result in loose
pins. It is not the same pins every time either, so it does not appear
to be related to the ground planes. This is a 14 layer .062 board.
The questions:
1. Any obvious remedies to eliminate the problem?
2 Anyone with similar experience?
3. How do you like my pictures?. I am trying out a new tool. This pics
are at 45X.
--
Leif Erik Laerum
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|