Hi Harris,



One of the major differences is that you shouldn't worry about Au embrittlement with immersion Au plating



Regards,



Vladimir

SENTEC

------Original Message------

From: Harris Dy

Sender: TechNet

To: [log in to unmask]

ReplyTo: TechNet E-Mail Forum

ReplyTo: Harris Dy

Sent: Jun 10, 2009 13:31

Subject: [TN] Immersion Gold versus Electrolytic Gold



Hi guys,

 

Can you please help to differentiate the two surface finishes? Also, is Electrolytic Gold done in Cu-Ni-Au plating line or there is another way?

 

Thanks in advance,

Harris





 





      



---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0

To unsubscribe, send a message to [log in to unmask] with following text in

the BODY (NOT the subject field): SIGNOFF Technet

To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)

To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest

Search the archives of previous posts at: http://listserv.ipc.org/archives

Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815

-----------------------------------------------------







SENTEC

11 Canadian Road, Unit 7.

Scarborough, ON M1R 5G1

Tel: (416) 899-1882

Fax: (905) 882-8812

www.sentec.ca


ATOM RSS1 RSS2