Bev

I have never tried lead free solders with nickel, but my experience with tin lead was a disaster. Years ago a "noted soldering expert" suggest that nickel coated features on PCBs would be all the rage.  Fortunately we found early on in some lab experiments it passivates  in half a heart beat. Some others were less fortunate.

Best regards
Lee
J. L. Parker Ph. D.
JLP Consultants LLC
804 779 3389
  ----- Original Message ----- 
  From: Bev Christian<mailto:[log in to unmask]> 
  To: [log in to unmask]<mailto:[log in to unmask]> 
  Sent: Wednesday, May 06, 2009 7:41 PM
  Subject: [TN] Nickel - again


  Technetters,
  Have any of you had any experience with trying to solder tin-based solders
  to uncoated nickel?  What kind of flux did you use?  Do you know if the
  joints had long term reliability, not just appearing to be "strong" joints
  right after formation?  What about negative wetting angles causing possible
  stress concentration points?
  Bev
  RIM

  ---------------------------------------------------
  Technet Mail List provided as a service by IPC using LISTSERV 15.0
  To unsubscribe, send a message to [log in to unmask]<mailto:[log in to unmask]> with following text in
  the BODY (NOT the subject field): SIGNOFF Technet
  To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET Technet NOMAIL or (MAIL)
  To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest
  Search the archives of previous posts at: http://listserv.ipc.org/archives<http://listserv.ipc.org/archives>
  Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16<http://www.ipc.org/contentpage.asp?Pageid=4.3.16> for additional information, or contact Keach Sasamori at [log in to unmask]<mailto:[log in to unmask]> or 847-615-7100 ext.2815
  -----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------