TECHNET Archives

April 2009

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
"Stadem, Richard D." <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Stadem, Richard D.
Date:
Wed, 29 Apr 2009 10:09:04 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (106 lines)
Wayne, of course you need to hold the part carefully when soldering the first pad. Refer to this tried and proven method  as listed in IPC 7711 Sec 5.3.1, like I stated in my first post.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Thayer, Wayne
Sent: Wednesday, April 29, 2009 9:32 AM
To: [log in to unmask]
Subject: Re: [TN] FW: Lead Free Reworking of Multilayer Ceramic Capacitors


 150C is a bit hot!  To get the caps up there, the other side of your board may well be at reflow.  We use 100-130C at the rework site

Richard's advice concerns me unless the part is glued down.  The tendency for the part to tombstone when soldering one side without any adhesive under the part is tremendous.  When it tries to tombstone, it will get sucked into contact with the iron.

If the pads are large enough (and most designs have pads that are too large as Werner and others have pointed out) then a trained operator using either two irons or the ones set up in tweezer fashion can, with appropriately sized tips, reflow both pads simulataneously without tombstoning the part.  Pre-heat always helps this process.

Wayne Thayer

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of bob wettermann
Sent: Wednesday, April 29, 2009 9:36 AM
To: [log in to unmask]
Subject: Re: [TN] FW: Lead Free Reworking of Multilayer Ceramic Capacitors

We would suggest using a hot plates to heat the caps to 150C which should allow for iron placement and soldering.  It's not the heat, it's the thermal gradient.

Regards

Bob Wettermann
BEST
www.solder.net
PH 847-767-5745




________________________________
From: "Stadem, Richard D." <[log in to unmask]>
To: [log in to unmask]
Sent: Wednesday, April 29, 2009 8:22:45 AM
Subject: Re: [TN] FW: Lead Free Reworking of Multilayer Ceramic Capacitors

Hi, James.
Yes, you CAN safely solder MLCCCs using a solder iron, but it is dependent on operator training and operator diligence. For hand soldering a MLCCC, have them flux and apply solder to one pad first, then place the part, melt the solder on that first pad by touching the PAD ONLY with the iron. Then solder the other side by again touching the pad only with the iron while adding a little wire solder. For water-soluble process, use flux if necessary. For no-clean soldering, do not use a liquid flux, you should be able to solder with only the flux contained in the wire core.

However, my experience has shown they should be trained to never use a tweezer style or U-shaped tip to solder the part in, as this thermally shocks the MLCCC directly and has proven to be the single biggest cause of cracked chips in a hand-solder or rework process. They can use a tweezer or U-shaped tip style to remove a chip cap or resistor that will not be re-used, but let's be practical, if the tweezer style iron is available, they will use it to place the part, hold it down with a pick, and release. That's what operators do. So don't allow the use of the tweezer style on any chip cap or resistor. Many of the chip resistors are also ceramic and they are also susceptible to this as well. Rather than have the operator need to look at a BOM to discern which chip caps are ceramic and which ones are not, we train them to use the pad doming method I described above (IPC 7711 section 5.3.2) on all chip caps/resistors, i.e., treat them all as being ceramic.

The methods described in IPC 7711 sections 3.3.1, 3.3.2, and 3.3.3 work well for removal, BUT ARE NOT INTENDED FOR REPLACEMENT. For replacement, I actually prefer using the hand-held hot air wand whenever possible because I was properly trained (to be a trainer) by a Master IPC trainer, and Replacement methods using the hot air wand are shown in sections 5.3.1 (don't be confused by the error where they describe solder paste but show wire solder being deposited) and 5.3.2, which is the point-to-point method I describe, except they show direct contact with the tip, which is not necessary.
The method shown in 5.3.1 really works if you follow the steps exactly as shown. The chip does not blow away. The trick is learning to adjust the hot air wand air flow and the two-stage distance to first properly dry the solder paste, then move in to reflow it. When the solder paste becomes liquid (thanks Werner) it holds the chip securely, it never blows away.

But you probably came to the same conclusion that I have, in that there are many circuit boards that simply can't get hot enough to use the hot air wand. So the indirect iron method seems to work well from an all around standpoint.

I would sure like to hear from others on the forum on this subject.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of James Liddle
Sent: Wednesday, April 29, 2009 3:01 AM
To: [log in to unmask]
Subject: [TN] FW: Lead Free Reworking of Multilayer Ceramic Capacitors

Hello

When carrying out a rework or repair of a RoHS Compliant PWA, I have been using Lead Free Solder, Alloy Designation SAC 305, RS Stock Number 445-5858, for Hand Soldering operations.  Given that Lead Free Solder has a higher melting point than Tin Lead Solder, the Manufacturer of this has suggested that temperature of the Soldering Tip used in conjunction with it, should be between 350°C and 370°C for effective results.  However, with regards to Multilayer Ceramic Capacitors, this conflicts with the advice published on page 97 of AVX's Surface Mounting Guide, which recommends Hot Air Reflow as the preferred rework method; and to a lesser extent, section 3.3 of Yageo's MLCC Application Manual.

Given that in a lot of instances Hand Soldering is the only practical method, does anyone know of a technique where it can safely be employed for Multilayer Ceramic Capacitor rework, using Lead Free Solder?

Thanks

James Liddle
_________________________________________________________________
Beyond Hotmail - see what else you can do with Windows Live.
http://clk.atdmt.com/UKM/go/134665375/direct/01/
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

This e-mail and any files transmitted with it may be proprietary and are intended solely for the use of the individual or entity to whom they are addressed. If you have received this e-mail in error please notify the sender.
Please note that any views or opinions presented in this e-mail are solely those of the author and do not necessarily represent those of ITT Corporation. The recipient should check this e-mail and any attachments for the presence of viruses. ITT accepts no liability for any damage caused by any virus transmitted by this e-mail.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2