TECHNET Archives

March 2009

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
"Whittaker, Dewey (EHCOE)" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Whittaker, Dewey (EHCOE)
Date:
Mon, 9 Mar 2009 09:03:16 -0700
Content-Type:
text/plain
Parts/Attachments:
text/plain (86 lines)
Richard,
I agree with you on the Eccobond and Resiweld having qualified them a
long time ago, but I am not aware of Armstrong C7. If you say it does a
bang-up job, I would be concerned since it's 3 levels higher than C4.
Seriously though does it pass for Aerospace work (outgassing, corrosion,
compatibility issues)? Let me know, as I don't want to appear as stuck
in the past.
Dewey 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Stadem, Richard D.
Sent: Monday, March 09, 2009 5:01 AM
To: [log in to unmask]
Subject: Re: [TN] Coatings, epoxies, etc crash course

Armstrong C7 with Hardener "W".
Resiweld
Eccobond
These all work well for sealing board cuts or damaged FR-4, but I like
the Armstrong best. 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Genny Gibbard
Sent: Friday, March 06, 2009 10:35 AM
To: [log in to unmask]
Subject: [TN] Coatings, epoxies, etc crash course

Hello all,
I do a lot of component and material sourcing, crossing, and spec'ing.
Probably the area I struggle with the most is the materials, like
epoxies for board repairs, or adhesives, or sealants, cleaners, etc
etc,...I did electrical engineering, not chemical.
Is there any good resource place to get a handle on when you want an
acrylic versus an epoxy, or silicone, or ... basic properties, what
environment they are needed for, etc.
A specific sourcing question I have right now - for challenging board
repairs we use specially trained operators in a rework cell that use a
2-part epoxy to repair FR4.  One product has a track cut, that usually
causes weave exposure, that happens on every board on the line to allow
for different configurations, and they want a way to protect it
adequately with a 1-part quick curing material without sending it to the
rework cell.  We've tried those conformal coat pens, and they can be
washed right off the board.  Any suggestions?

Genny 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2