What specific ionic cleanliness test should I have completed?  I'm told
there are several methods, with each giving different results.

Thanks for all the feedback up to this point!

Jim


Original Message:
-----------------
From: Karen Tellefsen [log in to unmask]
Date: Tue, 10 Mar 2009 07:43:29 -0500
To: [log in to unmask]
Subject: Re: [TN] Wrong flux used


Yuck!

The flux wicked up the wires, those wires will fail.  If the wires can be
replaced, you may be able to salvage the rest of the boards if you wash
them very thoroughly with hot DI water.  A prewash with saponifier wouldn't
hurt.  After washing,  you will need to ensure that all the flux was
removed by ionic cleaniless measurements or extraction and IC.

Good luck

Karen Tellefsen - Electrical Testing
[log in to unmask]




                                                                           
             Jim West                                                      
             <[log in to unmask]                                             
             M>                                                         To 
             Sent by: TechNet          [log in to unmask]                     
             <[log in to unmask]>                                          cc 
                                                                           
                                                                   Subject 
             03/09/2009 06:46          [TN] Wrong flux used                
             PM                                                            
                                                                           
                                                                           
             Please respond to                                             
              TechNet E-Mail                                               
                   Forum                                                   
             <[log in to unmask]>                                             
             ; Please respond                                              
                    to                                                     
                 Jim West                                                  
             <[log in to unmask]                                             
                    M>                                                     
                                                                           
                                                                           




During selective soldering, our operator used an IA flux (superior flux
75), which we normally use to dress up the soldering nozzle to create a
smooth flow of solder.  The flux was applied by a spray fluxer.  The
operator used the wrong bottle when reloading the spray fluxer.

We ran the boards through a wash system hoping to remove the IA flux.

The soldering operation involves discrete wires and I would think that the
flux would wick up under the wire insulation and not be reachable for
cleaning.

My questions are:

If the flux has wicked up under the wire insulator and can not be reached
by cleaning, will this type of flux
cause issues with the copper wire?

Will cleaning the boards be enough to say that no harm will be done, or
will this flux cause latent issues due to it's aggressiveness? (other
components were touched by this flux, i.e. SMT ceramic capacitors,
resistors)


Flux information
Superior soft soldering flux:
"The inorganic acid (IA) zinc chloride fluxes, commonly referred to as
"acid fluxes," are used for industrial soft soldering applications with
tin/lead, tin/silver, and other solder combinations. These fluxes typically
contain a combination of zinc chloride, hydrochloric acid, and ammonium
chloride and are used for soldering stainless steels, brass, copper, and
other metals."

Thanks,
Jim

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------


--------------------------------------------------------------------
mail2web.com – What can On Demand Business Solutions do for you?
http://link.mail2web.com/Business/SharePoint

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2