Doug - I am not familiar with dyne pens...can you explain?
I have also heard of a simpler test called the water break test. Literally
all you do is get a sample of DI water and pipette a few drops onto the PCB
surface. You are looking for the water to spread and wet to the PCB
surface, indicating it is free of contaminants. If it beads up (like on a
well waxed car), then it is indication of a film or contaminant that would
result in poor coating. I am not certain how different solder mask
materials effect the results of this test, but you can't argue the cost and
simplicity.
Kevin Glidden
Manufacturing Engineer
Luminescent Systems Inc.
-----Original Message-----
From: Douglas Pauls [mailto:[log in to unmask]]
Sent: Thursday, February 05, 2009 5:33 PM
To: [log in to unmask]
Subject: Re: [TN] Coating material
Ted,
Where do you see the dewetting and what processes come before coating?
In my experience, dewetting comes three general sources:
1. A problem with the surface energy of the component or solder mask.
This may be due to mold release agents or the slick nature of the plastic
itself. You want surface energies in excess of 40 dynes/cm. Surface
energies of 30-35 dynes/cm are a problem. I use Dyne Pens as a quick check.
Has there been a change in process or part supplier?
2. A problem with a barrier material. Again, it may be a mold release
agent, many of which are Teflon or sulfur based, or it may be a process
residue. Could be silicone residues, could be fingerprints, could be any
number of things from second or third shift.
3. Dewey Whittaker.
Doug Pauls
Rockwell Collins
Ted Tontis <[log in to unmask]>
Sent by: TechNet <[log in to unmask]>
02/05/2009 03:56 PM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to Ted Tontis
<[log in to unmask]>
To
[log in to unmask]
cc
Subject
Re: [TN] Coating material
We are experiencing de-wetting upon application. We are using a PVA coater
and using the same ratio, 1 to 1. The problem is that it is interment
within
the same lot making it difficult to pin down.
Samples of bare boards as well as boards that coated fine and ones that
coated poorly have been sent out to a lab for eval.
Ted
-----Original Message-----
From: Tom P. Hummel [mailto:[log in to unmask]]
Sent: Thursday, February 05, 2009 2:45 PM
To: TechNet E-Mail Forum; Ted Tontis
Subject: RE: [TN] Coating material
We currently use HumiSeal 1B73AP thinned 1 to 1 with 521 in our PVA
machine and have not had any issues. Are you experiencing problems?
What type of automated machine are you using?
Thomas P. Hummel
Carlton Industries Corp
[log in to unmask]
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|