I mentioned it just because in that particular case the lead finish
does affect the reliability of the joints.
--
Best regards,
Vladimir mailto:[log in to unmask]
SENTEC
11 Canadian Road, Unit 7.
Scarborough, ON M1R 5G1
Tel: (416) 899-1882
Fax: (905) 882-8812
www.sentec.ca
Well, what about Au-embrittlement? We know it causes earlier failures, is bad news,
and cannot be predicted--only avoided.
Werner
-----Original Message-----
From: Vladimir Igoshev <[log in to unmask]>
To: TechNet E-Mail Forum <[log in to unmask]>; Werner engelmaier <[log in to unmask]>
Sent: Mon, 9 Feb 2009 6:52 pm
Subject: Re[2]: [TN] lead adding
Well Werner, then what about Gold embrittlement?
--
Best regards,
Vladimir mailto:[log in to unmask]
SENTEC
11 Canadian Road, Unit 7.
Scarborough, ON M1R 5G1
Tel: (416) 899-1882
Fax: (905) 882-8812
www.sentec.ca
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|