Inge is absolutely right. Unfortunately, in the majority of
so-called "solderability" cases, people try to tweak the process and
not get to the root cause fo the problem. SEM/EDS is indefensible to
do it.
--
Best regards,
Vladimir mailto:[log in to unmask]
SENTEC
11 Canadian Road, Unit 7.
Scarborough, ON M1R 5G1
Tel: (416) 899-1882
Fax: (905) 882-8812
Hi Graham,
steam test does not tell you much about underlying platings. Namely, if you
are using ceramic PGAs, the pins are nickel plated Kovar with some gold
upon. I have seen something like yours a number of time. It has to do with
bad pretreatment before nickel plating, or bad nickel plating, which is not
uncommon these days. Even plastic PGAs can have bad underplate. My advice:
have a look at some cross sections in SEM/EDAX. Start with a glass fiber
brush (kind of eraser) stroke. If the nickel is anomalous, you'll see it in
a ordinary stereo microscope. If you are used to etching, a number of dips
in a not to concentrated HCl/H2SO4/H2O (strip gold at first of course) will
probably reveal a lot even before SEM. I have some pictures on this, if I
can find them, I'll send a pidgeon.
Ingewww.sentec.ca
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|