Hi Bob - does that mean you didn't have to pre-chill your orange juice for
breakfast? Most of us here in the Midwest had to thaw ours our in the
microwave! My guess is the Bev just had his as an orange-sickle.
Dave
"Croslin, Robert" <[log in to unmask]>
Sent by: TechNet <[log in to unmask]>
01/15/2009 08:50 AM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to
"Croslin, Robert" <[log in to unmask]>
To
[log in to unmask]
cc
Subject
Re: [TN] NTC RE: [TN] Possible cause on open
Whiners! It was all the way down to 39° last night here in Florida.
Bob Croslin
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bev Christian
Sent: Thursday, January 15, 2009 9:12 AM
To: [log in to unmask]
Subject: [TN] NTC RE: [TN] Possible cause on open
Beatcha!
-20C with no wind at 6 AM.
It's not called the Great White North for nothing!
Bev
RIM
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Thursday, January 15, 2009 8:05 AM
To: [log in to unmask]
Subject: Re: [TN] Possible cause on open
Mornin' Everbody!
Well, here in Tulsa, we're just like a lot of other people in the country
this morning, trying to stay warm. Right now we're sitting at -10 C. with
a wind chill of -15 C. It's supposed to be colder tomorrow...
GA, I have your pictures posted now. They're at:
http://stevezeva.homestead.com/files/Fracture1.jpg
http://stevezeva.homestead.com/files/Fracture2.jpg
Hopefully someone can give you some ideas...
Steve
________________________________
From: Tan Geok Ang [mailto:[log in to unmask]]
Sent: Wednesday, January 14, 2009 7:27 PM
To: [log in to unmask]; Steve Gregory
Subject: Possible cause on open
Hi Steve,
Please help to download these pictures TechNet, thanks.
Hi All experts,
Testing (combine test of 16G at 85 oC) was performed on
evaluation boards with under-filled BGAs. Open issue (cracks) was
detected only at some corners of the BGA (35x35mm with 1156 balls) after
the test. Lead-free process and PCB with ENIG surface finish. Peak
temperature is 248 oC with a 65 sec above 217 oC.
FYI, the service lab has not come out a report.
What are the possible causes? (CET mismatches, Lead-free
alloy related, material, processes)
Thank you in advance.
Regards
GA Tan
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential
information, privileged material (including material protected by the
solicitor-client or other applicable privileges), or constitute non-public
information. Any use of this information by anyone other than the intended
recipient is prohibited. If you have received this transmission in error,
please immediately reply to the sender and delete this information from
your system. Use, dissemination, distribution, or reproduction of this
transmission by unintended recipients is not authorized and may be
unlawful.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|