Date:
Wed, 21 Jan 2009 08:39:09 +0800
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, Tan Geok Ang <[log in to unmask]>
Subject:
From:
Tan Geok Ang <[log in to unmask]>
Content-Transfer-Encoding:
quoted-printable
In-Reply-To:
Content-Type:
text/plain; charset="us-ascii"
MIME-Version:
1.0
Parts/Attachments:
text/plain (81 lines)
Hi Steve,
		It looks to me that you are using no-clean flux though
you mentioned DI washes (water base flux).
While it seems to me more like a delamination at the screw nut area.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of [log in to unmask]
Sent: Wednesday, 21 January 2009 3:59 AM
To: [log in to unmask]
Subject: Re: [TN] Strange Mask Appearance

Steve- I'm probably the culprit that put that report on TN long ago- and

again recently. Liquid solder masks often use fumed silica as
filler/thickener  
to keep it in place. This is often sold under the Cab-O-Sil tradename.  
Aggressive cleaning agents can dissolve off part of the under or un
cured solder  
mask polymer, exposing the while silica filler. When you heat the
undercured  
mask, it will soften and allow the filler to sink down into the polymer,
so the  
solder mask all looks green again. 
Re the curing from wave solder, this may not work if you are working
with a  
UV cured mask. That's why it is important to monitor the output of UV
lamps,  
which not all shops do, thinking that UV lamps behave the same as
incandescent 
 lamps- which they don't. 
Yes, the heat gun is a very inexpensive $0.05 test, quick, easy and
requires 
no instrumentation. 
 
(Steve- I have some photos of the differences between one, two and three

passes under UV lamps to show the difference if you'd like them. If so,
pls give  
me a mailing address.)  

Bill  Kenyon
Global Centre Consulting
3336 Birmingham Drive
Fort Collins, CO  80526
Tel: 970.207.9586   Cell:  970.980.6373

**************A Good Credit Score is 700 or Above. See yours in just 2
easy 
steps! 
(http://pr.atwola.com/promoclk/100000075x1215855013x1201028747/aol?redir
=http://www.freecreditreport.com/pm/default.aspx?sc=668072%26hmpgID=62%2
6bcd=De
cemailfooterNO62)

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2