Subject:
From:
"Stadem, Richard D." <[log in to unmask]>
Reply To:
(Leadfree Electronics Assembly Forum)
Date:
Thu, 4 Dec 2008 16:55:25 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (146 lines)
I have to agree with what George said, but I can tell you that I have a
lot of experience with IAg boards, including super large ones that were
40" wide by 24" high and weighed 75 lbs. I have never had any issues
with it, and I have been an advocate for IAg for many years. However, I
understand that sometimes ENIG is the proper choice, and also
applications where neither one is practical.

As far as why many still use ENIG, here are some reasons I have been
told:
	1. Because it is easier to solder to gold (BS, you don't solder
to the gold)
	2. Because you get a better solder joint soldering to gold (BS,
with ENIG you are soldering to the nickel
underneath)
	3. Because you need the added strength of the nickel plating in
the vias (in some applications, true).
	4. It costs more, so it must be more reliable (Absolute BS)
	5. It performs better in high impedance, high frequency circuits
than IAg (Absolute BS, the opposite is in fact 		   generally
true)
	6. Well, we always have used ENIG, and we just boilerplate the
requirements from fab drawing to new fab drawing (I 	   have had so
many design engineers tell me this)
	7. We need the gold for contact switches or wirebonding purposes
(true).
	8. IAg does not solder well after 6 months (BS, it is easier to
form a good SJ with the copper underneath provided 	   you have
packaged and stored the IAg boards properly in the first place).
	9. We have always used ENIG from a particular PWB vendor without
any issues, and are hesitant to change. (That's a 	   darn good
reason!)  

-----Original Message-----
From: Leadfree [mailto:[log in to unmask]] On Behalf Of Wenger, George M.
Sent: Thursday, December 04, 2008 3:52 PM
To: [log in to unmask]
Subject: Re: [LF] Pro's and Con's of using Immersion Silver

Tim,

We've used IAg since 1996 and have had extremel


Tim,

We've used IAg since 1996 and have had extremely good results.  You're
probably going to get all kinds of answers about solderability, storage,
and long term reliability but my short answer is that from my
prospective the solderability and long term reliability is better than
ENIG and the storage can be as good if you be careful where you store
it.

As for the question of why there are still a lot of companies using
ENIG, the best answers will come from those who are still using it.  It
is a good, flat solderable surface and as long as you don't run into a
problem with solder joint failures there is probably not a lot of reason
to change to an alternative.  However,  I assume there are also lots of
companies who had problems with ENIG that have switch to IAg.

Regards,
George
George M. Wenger
Andrew Wireless Solutions
Senior Principal FMA / Reliability Engineer 40 Technology Drive, Warren,
NJ 07059
(908) 546-4531 [Office]  (732) 309-8964 [Cell] [log in to unmask]
 

-----Original Message-----
From: Leadfree [mailto:[log in to unmask]] On Behalf Of Tim Boyer
Sent: Thursday, December 04, 2008 3:16 PM
To: [log in to unmask]
Subject: [LF] Pro's and Con's of using Immersion Silver

Currently we use Immersion Gold for our ROHS boards.

We are looking into changing to Immersion Silver.

What differences are there in solderability, storage, long term
reliability, operating temperatures,

etc?

Why are allot of companies still using Immersion Gold over Nickel for
ROHS boards?

 

Tim Boyer, CID+


------------------------------------------------------------------------
-------Leadfee Mail List provided as a service by IPC using LISTSERV
1.8d To unsubscribe, send a message to [log in to unmask] with following
text in the BODY (NOT the subject field): SIGNOFF Leadfree To
temporarily stop/(start) delivery of Leadree for vacation breaks
send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives Please
visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
------------------------------------------------------------------------
-------


No virus found in this incoming message.
Checked by AVG - http://www.avg.com
Version: 8.0.176 / Virus Database: 270.9.13/1828 - Release Date:
12/4/2008 8:05 AM
------------------------------------------------------------------------
------------------------
This message is for the designated recipient only and may contain
privileged, proprietary, or otherwise private information.  
If you have received it in error, please notify the sender immediately
and delete the original.  Any unauthorized use of this email is
prohibited.
------------------------------------------------------------------------
------------------------
[mf2]


------------------------------------------------------------------------
-------Leadfee Mail List provided as a service by IPC using LISTSERV
1.8d
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks
send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
------------------------------------------------------------------------
-------

-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------

ATOM RSS1 RSS2