Fri, 5 Dec 2008 15:11:25 -0500
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, Werner engelmaier <[log in to unmask]>
Subject:
From:
Werner engelmaier <[log in to unmask]>
Content-Type:
text/plain; charset="utf-8"
In-Reply-To:
Content-Transfer-Encoding:
quoted-printable
MIME-Version:
1.0
Parts/Attachments:
text/plain (397 lines)
 Hi Arnaud,
A BGA with an attached heatsink is causing the BGA to be thermally unsymmetrical--and you get warpage by the 'bimetallic strip' effect.
I show some nice shadow moire pictures [courtesy Advanced Semiconductor Engineering Inc.] showing 9 mils of warpage fro 20 to 240°C in my workshops.

Werner


 


 

-----Original Message-----
From: Arnaud Grivon <[log in to unmask]>
To: Werner engelmaier <[log in to unmask]>
Sent: Fri, 5 Dec 2008 9:21 am
Subject:  Re: [TN] 答复: Re: [TN] BGA soldering open issue









Hello Werner, 
 

Could you please elaborate on your posting stating that BGAs with 
heatsinks are more prone to warpage during assembly? 

Are you thinking of cavity down BGA (such as SBGA), FC-PBGA, or...? 

Would you have any publication/article to share? 

I thank you in advance for your support. 

Best regards, 
 

Arnaud Grivon 
 

Werner engelmaier a écrit : 

>  Nee hao Hechong, 

> BGAs with heatsinks have been shown to warp and thus loading the SJs in tension. 

> 

> Werner 

> 

> 

>  
> 

> 

>  
> 

> -----Original Message----- 

> From: Cong He <[log in to unmask]> 

> To: [log in to unmask] 

> Sent: Thu, 4 Dec 2008 10:08 pm 

> Subject:  [TN] 答复: Re: [TN] BGA soldering open issue 

> 

> 

> 

> 

> 

> 

> 

> 

> 

> 

> surface fin
ish is hasl. 
> 

> after analysed parts of the board, we found some balls of the bga rupture. 

> Could it be the material of the ball(BGA) cause the problem? 

> 

> by the way, there is a heatsink which is double size lager than the chip 
> stick on it without other fixture. 

> will the heatsink be the reason? 

> 

> 

> 

> 

> 

> 

> Hechong 

> 

> 

> 

> 

> 

> "Wenger, George M." <[log in to unmask]> 
> 发件人:  TechNet <[log in to unmask]> 

> 2008-12-05 10:57 

> 请答复 给 

> TechNet E-Mail Forum <[log in to unmask]>; 请答复 给 

> "Wenger, George M." <[log in to unmask]> 

> 

> 

> 收件人 

> [log in to unmask] 

> 抄送 

> 

> 主题 

> Re: [TN] BGA soldering open issue 

> 

> 

> 

> 

> 

> 

> What is the surface finish on your PCBA? 

> 

> 

> 

> Necong, 

> 

> What is the surface finish on your PCBA? 

> 

> Regards, 

> George 

> George M. Wenger 

> Andrew Wireless Solutions 

> Senior Principal FMA / Reliability Engineer 

> 40 Technology Drive, Warren, NJ 07059 

> (908) 546-4531 [Office]  (732) 309-8964 [Cell] 

> [log in to unmask] 

>  
> 

> -----Original Message----- 

> From
: TechNet [mailto:[log in to unmask]] On Behalf Of Cong He 

> Sent: Thursday, December 04, 2008 9:09 PM 

> To: [log in to unmask] 

> Subject: [TN] BGA soldering ope 

> n issue 

> 

> dear all: 

> 

> I am facing a problem of bga soldering. 

> 

> when the board have just soldered ,it pass all test. 

> But after sometime, maybe for a few weeks, 

> some of the bga balls opened. the function became normal if i press the 
> chip on the top side. 

> 

> It seems that the pcb didn't warp much,it seems even no warp at all. 

> Does any of you know why? And how to improve? 
> 

> 

> 

> 

> 

> 

> Hechong 

> 

> --------------------------------------------------- 

> Technet Mail List provided as a service by IPC using LISTSERV 15.0 

> To unsubscribe, send a message to [log in to unmask] with following text 

> in 

> the BODY (NOT the subject field): SIGNOFF Technet 

> To temporarily halt or (re-start) delivery of Technet send e-mail to 

> [log in to unmask]: SET Technet NOMAIL or (MAIL) 

> To receive ONE mailing per day of all the posts: send e-mail to 

> [log in to unmask]: SET Technet Digest 

> Search the archives of previous posts at: 

> http://listserv.ipc.org/archives 

> Please visit IPC web site 

> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional 

> information, or contact Keach Sasamori at sasako@
ipc.org or 847-615-7100 

> ext.2815 

> ----------------------------------------------------- 

> 

> 

> No virus found in this incoming message. 

> Checked by AVG - http://www.avg.com 
> Version: 8.0.176 / Virus Database: 270.9.13/1828 - Release Date: 

> 12/4/2008 8:05 AM 

> ------------------------------------------------------------------------------------------------ 

> This message is for the designated recipient only and may 

> contain privileged, proprietary, or otherwise private information. 
> If you have received it in error, please notif 

> y the sender 

> immediately and delete the original.  Any unauthorized use of 

> this email is prohibited. 

> ------------------------------------------------------------------------------------------------ 

> [mf2] 

> 

> 

> --------------------------------------------------- 

> Technet Mail List provided as a service by IPC using LISTSERV 15.0 

> To unsubscribe, send a message to [log in to unmask] with following text in 

> the BODY (NOT the subject field): SIGNOFF Technet 

> To temporarily halt or (re-start) delivery of Technet send e-mail to 
> [log in to unmask]: SET Technet NOMAIL or (MAIL) 

> To receive ONE mailing per day of all the posts: send e-mail to 
> [log in to unmask]: SET Technet Digest 

> Search the archives of previous posts at: http://listserv.ipc.org/archives 

> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 
> for additional information, or contac
t Keach Sasamori at [log in to unmask] or 
> 847-615-7100 ext.2815 

> ----------------------------------------------------- 

> 

> 

> 

> 

> 

>  
> 

> 

> --------------------------------------------------- 

> Technet Mail List provided as a service by IPC using LISTSERV 15.0 

> To unsubscribe, send a message to [log in to unmask] with following text in 

> the BODY (NOT the subject field): SIGNOFF Technet 

> To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) 

> To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest 

> Search the archives of previous posts at: http://listserv.ipc.org/archives 

> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815 

> ----------------------------------------------------- 

>   


 


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2