Sender:
X-To:
"Igoshev, Vladimir" <[log in to unmask]>, TechNet E-Mail Forum <[log in to unmask]>
Date:
Wed, 20 Aug 2008 14:25:33 -0400
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, Joyce Koo <[log in to unmask]>
Subject:
From:
Joyce Koo <[log in to unmask]>
content-transfer-encoding:
quoted-printable
In-Reply-To:
Content-Type:
text/plain; charset="us-ascii"
MIME-Version:
1.0
Parts/Attachments:
text/plain (135 lines)
Sorry, should be FIB...need more coffee...jk

-----Original Message-----
From: Igoshev, Vladimir [mailto:[log in to unmask]] 
Sent: Wednesday, August 20, 2008 2:23 PM
To: TechNet E-Mail Forum; Joyce Koo
Subject: RE: [TN] Diffuse topic

There is NO WAY it was ion milling. Just look at the huge directional
scratches on the surface :-)

Vladimir

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Joyce Koo
Sent: Wednesday, August 20, 2008 2:19 PM
To: [log in to unmask]
Subject: Re: [TN] Diffuse topic

(1) is it done by ion milling?  You might have carried over sputtering.
(2) excessive grain boundary diffusion might be the case.  The structure
looks grainy (not layer by layer growth...).  Possibly too high of
current density (not enough time for atom to diffuse along the
surface...). Is the surface very rough? 
 
Good luck..  
              My 1.86 cents

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Wednesday, August 20, 2008 8:00 AM
To: [log in to unmask]
Subject: Re: [TN] Diffuse topic

Mornin' Inge!

Got your picture up! Go to:

http://stevezeva.homestead.com/files/Nickel_Diffusion.jpg

Steve

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Hernefjord Ingemar
Sent: Wednesday, August 20, 2008 5:08 AM
To: [log in to unmask]
Subject: [TN] Diffuse topic

Investigation of coax Kovar/glass feed thrues soldered to nickel plated
metal bodies gave, that nickel from the feed thrue's barrel nickel
plating diffused as much as 38 micrometers (!)into the tin from the
tin/lead solder during the vapour phase soldering. Nickel had diffused
from both the feedthrue and the package.  How is that possible? Thought
polish smear gave false picture, but the analyst claims that what you
see is true nickel diffusion and nickel/tin IMCs. I'll ask dr Gregory
for help with a photo for  you all. The sample you will see is exposed
more than normal to an etchant to prove that smear is not the
case..start from the bottom shows nickel (black), nickel IMCs (greyish)
and topmost tin (bright). There is nearly no lead present.

Inge

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential
information, privileged material (including material protected by the
solicitor-client or other applicable privileges), or constitute
non-public information. Any use of this information by anyone other than
the intended recipient is prohibited. If you have received this
transmission in error, please immediately reply to the sender and delete
this information from your system. Use, dissemination, distribution, or
reproduction of this transmission by unintended recipients is not
authorized and may be unlawful.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------



---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential information, privileged material (including material protected by the solicitor-client or other applicable privileges), or constitute non-public information. Any use of this information by anyone other than the intended recipient is prohibited. If you have received this transmission in error, please immediately reply to the sender and delete this information from your system. Use, dissemination, distribution, or reproduction of this transmission by unintended recipients is not authorized and may be unlawful.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2