We reflowed thousands of these very same caps in different products in a
previous life, and I don't recall any problems with them from an
operating or reliability standpoint. But that was with a MRT of around
230 deg. C, and a TAL of about 60 seconds.
The bigger problem with them was handling.
Because the two leads coming out from the bottom of the can puts it on a
center fulcrum, any operator who puts their fingers or thumbs on the top
of these cans and rocks them even slightly when handling the assembly
will cause the pads to lift right off of the board. We had to train and
retrain the operators not to touch these parts.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Ioan Tempea
Sent: Tuesday, July 22, 2008 9:45 AM
To: [log in to unmask]
Subject: [TN] Lead-free soldering of electrolytic caps
Dear Technos,
I need to solder these babies, see
http://www.panasonic.com/industrial/components/pdf/PIC_FK_SERIES.pdf on
lead-free. We're on SAC305.
Please check the last page of the spec, series EEV-Q and EEV-M, the big
cans. I must say that Panasonic does not really help us assemblers by
labelling the parts as being RoHS compliant; they might not have the
banned stuff in them, but they are anything but high-temp. When
designers see RoHS compliant, it's case closed for them and open issues
for us.
How are you guys getting around the poor temperature rating of the
component? Would the cool caps work? Are you soldering them manually?
Should I bother studying the Bi alloys?
Thank you,
Ioan
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|