Do you meet the requirements as below?

Ingemar Hernefjord

http://www.pcbpro.com/ipc-inspection.php



-----Ursprungligt meddelande-----
Från: TechNet [mailto:[log in to unmask]] För Jack Olson
Skickat: den 7 februari 2008 18:32
Till: [log in to unmask]
Ämne: Re: [TN] FAB: Thin Trace Failures

By recommending furthur polishing, are you saying it would be helpful to
know if the void is circular? So if the void gradually goes away it means we
might have just hit it  in the "fat" part, but there might really be enough
copper to consider it a good trace? I'm not so familiar with these type of
conditions, but several responses seemed to indicate that this might be
okay, but we have over 50% assemblies failing final test when we heat them
up. (which is not okay)

Jack


On 2/7/08, Igoshev, Vladimir <[log in to unmask]> wrote:
>
> I have (at least something similar). Try to polish it a bit more and it
> will either go away. Or become a "complete" trace (depending on how
> deep-in it has been already polished).
>
> Vladimir
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Jack Olson
> Sent: Thursday, February 07, 2008 10:33 AM
> To: [log in to unmask]
> Subject: [TN] FAB: Thin Trace Failures
>
> Has anyone ever seen a cross-section like this?
>
> http://www.frontdoor.biz/PCBportal/opentrace.jpg
>
> (ignore the words on the pic, just a guess)
>
> Can you point me in the right direction for cause?
>
> thanks,
> Jack
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 15.0
> To unsubscribe, send a message to [log in to unmask] with following text
> in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
> http://listserv.ipc.org/archives
> Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
> ext.2815
> -----------------------------------------------------
>
>
>
>
>

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------