Hi David,
Macro-voids [micro-voids is a different story, however] as a whole do not
increase the threat to reliability—this has been shown both with analysis and
testing. This is true for voids caused by gaseous inclusion or for shrinkage
voids [shrinkage voids existed long before LF-solders, but were rarely observed
because nobody was looking for them and they were all internal]. Indeed, in
ductile materials, voids have ablunting effect on crack propagation. however, the
effect is highly localized because of the 3D-goemetry of the SJs and has no
significant impact on SJ reliability.
Most of what is now called 'shrinkage voids' are more properly called
'shrinkage fissures' or 'hot tearing', and even 'fillet liftying,' 'pad lifting' and
'fillet cracking' are related.
There may indeed be special circumstances, where there is a possible
reliability impact, but I have not seen one as yet.
Werner
**************
Ideas to please picky eaters. Watch video on AOL Living.
(http://living.aol.com/video/how-to-please-your-picky-eater/rachel-campos-duffy/
2050827?NCID=aolcmp00300000002598)
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|