Hi,

Recently one of our motherboard failed. It reaches very high temperature
that melts the copper and explodes shooting (from the side of the board)
the melt copper to over 20 cm. the shooting hole cause delamination of
the board in the area. A lot of black smoke and was also seen. The max
voltage of the board is about 50V. The board worked fine for more then a
year. What could be the failure mechanism? Could it be due to conductive
filament formation (although the PCB should be free of that)?

Thanks

Gil Zilber
Elta Systems

 The information contained in this communication is proprietary to Israel Aerospace Industries Ltd. 
and/or third parties, may contain classified or privileged information, and is intended only for 
the use of the intended addressee thereof. If you are not the intended addressee, please be aware 
that any use, disclosure, distribution and/or copying of this communication is strictly prohibited.
If you receive this communication in error, please notify the sender immediately and delete it from 
your computer. Thank you. 


This message is processed by the PrivaWall Email Security Server. 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------