TECHNET Archives

August 2007

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Bev Christian <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Bev Christian <[log in to unmask]>
Date:
Fri, 31 Aug 2007 07:34:28 -0400
Content-Type:
text/plain
Parts/Attachments:
text/plain (75 lines)
Inge,
I'm not a wafer guys, but here are a couple of thoughts:
1) You don't say whether there is anything else laid down on the base
surface where the substrates are laid.  We tried using a similar mix at
Nortel to look at "fluxless soldering", but abandoned it because of ESD
issues.  
2) Silver oxide itself is still conductive so if the epoxy is heavily
loaded there is a good chance there is some of the oxide on the crisped
surface and since it is conductive couldn't it also form dendrites in
the right conditions of humidity and potential charge?

Bev
RIM

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Hernefjord Ingemar
Sent: Friday, August 31, 2007 4:53 AM
To: [log in to unmask]
Subject: [TN] Plasma "oxidation"

 
Yup. Strange title. I've been asked about a strange process, which one
was introduced without my knowledge, and I'm going to throw it out. But
I thought of consulting TN before. This is the case:

LTCC substrates are silver epoxy dispensed for chip mounting. In order
to avoid risk for silver migration, a guy invented plasma "oxidation",
i.e. he use a plasma cleaner, runs Argon with 6% Oxygen for a couple of
minutes on mounted substrates. The silver epoxy dots become blackish
because of oxidation, and oxidized epoxy is meant to minimize risk for
silver migration. The oxide is of course just nanometer thick. The guy
worked at a wafer manufacturing plant and had experience of cleaning
procedures.

I mean that this process is nonsense. If humidity gets in and condense
on the substrate, and if the electric field is high enough, and if there
are salts or contaminations, there is still enough silver to start
migration. Oxidation of the silver dot's surface is meaningless. Anyone
heard of such a strange process? Plasma operation on mounted LTCC
substrates is foreign to me, I want it out.

TrikeMan?

Inge

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential information, privileged material (including material protected by the solicitor-client or other applicable privileges), or constitute non-public information. Any use of this information by anyone other than the intended recipient is prohibited. If you have received this transmission in error, please immediately reply to the sender and delete this information from your system. Use, dissemination, distribution, or reproduction of this transmission by unintended recipients is not authorized and may be unlawful.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2