Dear all,
We are using the lead-free SN100C solder alloy for wave soldering. We
are experiencing wetting problems each time we have to solder a thick
board or a board with a large ground plane. I think that maybe we are
not using the right flux.
I would like to know which flux could give me good results with this
alloy? Also I would like to know if there are other manufacturers that
have same problems as ours.
Dominic
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------