Hello,
Thank you for the point in the right direction !!
The reason I am asking is because we have some boards with BGA memory.
There are 4 devices on one side of the PCB in very close proximity and 4
more directly underneath the top 4.
So, in an area 5cm x 1.5cm x .5cm of this PCB I have 8 microBGAs which X
amount of them are failing because of cold solder. Other people's wisdom is
to rework the BGAs one at a time but my concern is exposing such a small
area to lead-free temperatures up to 8 times.
I would imagine with 1 mil or 800 micron via thickness that the z-axis
stresses would be too much for 8 reflow cycles so I am trying to argue the
point of reworking (or replacing) at least 2 BGAs at a time.
Thank you,
David Tremmel
-----Mensaje original-----
De: TechNet [mailto:[log in to unmask]] En nombre de Hfjord
Enviado el: Friday, June 08, 2007 3:09 PM
Para: [log in to unmask]
Asunto: [TN] SV: [TN] Z-axis expansion
All you need is to say 'Thank you' to Tom Buck at DDI.
His paper tells you ALL about what you're asking for.
http://www.smta.org/files/SMTA_Boston_pbfree_ddi.pdf
By the way, why do you ask?
Inge
-----Ursprungligt meddelande-----
Från: TechNet [mailto:[log in to unmask]] För David Tremmel
Skickat: den 8 juni 2007 21:13
Till: [log in to unmask]
Ämne: [TN] Z-axis expansion
Hello,
I have seen comments regarding z-axis expansion that boards and
components
experience during reflow; would any of the gurus care to give some
numbers?
Such as the copper in the vias has such-and-such expansion versus a High
Tg
FR4 which has such-and-such z-axis expansion. (I am sure someone is
going
to correct me because I did not use the correct terms).
Thank you in advance,
David Tremmel
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|