Steve Gregory <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Steve Gregory <[log in to unmask]>
Date:
Fri, 4 May 2007 13:45:14 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (67 lines)
Hi Inge!

Got your pictures posted. Took me a bit, I was swapping our wave
solderpot from 63/37 to HMP. Done now. I'm getting quicker, I can do it
in 20-minutes now. Took me about 45-minutes when I first did it...

Anyways, here's the links:

http://stevezeva.homestead.com/files/Pic1.jpg
http://stevezeva.homestead.com/files/Pic2.jpg
http://stevezeva.homestead.com/files/Pic3.jpg
http://stevezeva.homestead.com/files/Pic4.jpg
http://stevezeva.homestead.com/files/Pic5.jpg
http://stevezeva.homestead.com/files/Pic6.jpg

-Steve-

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Hfjord
Sent: Friday, May 04, 2007 12:22 PM
To: [log in to unmask]
Subject: [TN] Metalurgists, need assistance

Have an issue with (randomly) lifted FPGA leads.
Pic 1: good joint after pull test
Pic 2: ditto but high magnification
Pic 3: "rotten" joint after pull test
Pic 4: ditto but high magnification
Pic 5: "rotten" cross section
Pic 6: ditto but high magnification

60Sn on ENIG, obviously a brittle region. Suspect Kirkendall voids, but
the pockets with zillions of Tin spheres (0.1 to 2 um in size) points at
insufficient peak temperature to make 100% melt and good solidifying. If
these little balls were Lead, I could understand, but they are Tin!
Never seen like. Any "quickhead" out there, need fast advice. 

Note: Pic 2, you can see the underlying board pad nickel as dark areas. 
An experienced analyst will hopefully recognize. No Phosphorous peaks!

My Friday headache.

Inge

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2