Hard or soft does not matter in a diffusion point of view. Hard gold
means it's alloyed, which is not the same as a chemical reaction with a
product that has different properties than the original elements. So,
doped or not doped Gold, the diffusion of gold in Tin will take place,
the gold atoms are free to move. This question comes repetedly, so I'll
send the ternary isopleth for Steve's wall, so that everyone can see the
Wt% vs alloys.
Inge
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Dan Skweres
Sent: den 24 maj 2007 17:25
To: [log in to unmask]
Subject: [TN] Gold content in solder joints
Question for you folks.... I'm aware of embrittlement issues with too
much gold in solder joints. The question came up here whether or not
there is a difference between "hard" gold content verses "soft" gold
content? Thanks in advance!
Dan
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|