Hi inge,
There are no pictures :-)
Regards,
Vladimir
AMD
-----Original Message-----
From: TechNet
To: [log in to unmask]
Sent: Fri May 04 13:21:47 2007
Subject: [TN] Metalurgists, need assistance
Have an issue with (randomly) lifted FPGA leads.
Pic 1: good joint after pull test
Pic 2: ditto but high magnification
Pic 3: "rotten" joint after pull test
Pic 4: ditto but high magnification
Pic 5: "rotten" cross section
Pic 6: ditto but high magnification
60Sn on ENIG, obviously a brittle region. Suspect Kirkendall voids, but
the pockets with zillions of Tin spheres (0.1 to 2 um in size) points at
insufficient peak temperature to make 100% melt and good solidifying. If
these little balls were Lead, I could understand, but they are Tin!
Never seen like. Any "quickhead" out there, need fast advice.
Note: Pic 2, you can see the underlying board pad nickel as dark areas.
An experienced analyst will hopefully recognize. No Phosphorous peaks!
My Friday headache.
Inge
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|